The search for selective heterogeneous catalysts for the aerobic oxidation of alcohols to ketones and aldehydes has drawn much attention in the last decade. To that end, different palladium-based catalysts have been proposed that use various organic and inorganic supports. In addition, supports that originate from a biological and renewable source that is also nontoxic and biodegradable were found to be superior. We heterogenized palladium chloride or acetate complexes with triphenylphosphine trisulfonate on iota-carrageenan xerogel by simple mixing of the complex and the polysaccharide in water. The resulting polysaccharide-catalyst mixture then underwent deep freeze and lyophilization, after which the catalyst was characterized by TEM, XPS and SEM-EDS and tested in aerobic oxidation. The new heterogeneous catalysts were successfully used for the first time in the aerobic oxidation of benzylic alcohols. Moreover, they were easily removed from the reaction mixture and recycled, yielding an increase in activity with each subsequent reuse. As determined by TEM and XPS, the reduction in palladium and the formation of nanoparticles during the reaction in ethanol yielded more active species and, therefore, higher conversion rates. A SEM-EDS analysis indicated that the palladium was thoroughly dispersed in the xerogel catalysts. Moreover, the xerogel catalyst was observed to undergo a structural change during the reaction. To conclude, the new heterogeneous catalyst was prepared by a simple and straightforward method that used a non-toxic, renewable and biodegradable support to yield an active, selective and recyclable heterogeneous system.

Palladium acetate that was heterogenized together with triphenylphosphine trisulfonate ligand on renewable polysaccharides was employed in the aerobic oxidation of benzyl alcohol in three representative solvents-hexane, ethyl acetate, and ethanol. Solvent polarity was found to affect the reaction rate, as both the solubility of benzyl alcohol and oxygen depend on the nature of the solvent. The conversion rate was decreased in the order of hexane > ethanol > ethyl acetate (conversion rates in the presence of the heterogenized iota-based catalyst after 24 h of reaction were 38, 20, and 15%, respectively). In addition, the nature of the polysaccharide, that is, the type and numbers of functional groups on its backbone, also affected the reaction

In the heterogeneous catalyst i-Pd(OAc)2(TPPTS)2, Pd(II) was reduced to Pd(0) by using different alcohol solvents, and the catalyst’s activity was studied in the aerobic oxidation of benzyl alcohol. We studied the effects of the impregnation time in ethanol as a solvent and the use of various alcoholic solvents on the size of palladium nanoparticles. We found that the reduction of palladium by the various alcohols yielded palladium nanoparticles that were active in the aerobic oxidation of benzyl alcohol. As determined by DLS, TEM, and zeta potential analyses, both the impregnation time in ethanol and the type of alcohol used were observed to affect nanoparticle formation, particle size distribution, and agglomeration, as well as the conversion rate. The palladium nanoparticles’ hydrodynamic diameter sizes obtained during the 24 h of impregnation time were in the range of 10–200 nm. However, following 24 h of impregnation in ethanol the nanoparticles tended to form aggregates. The conversion rates of all the primary alcohols were similar, while for secondary alcohol, in which the hydrogen of the hydroxyl is less acidic and there is steric hindrance, the conversion was the lowest. Performing the oxidation using the solvent 1-propanol yielded smaller nanoparticles with narrower distributions in comparison to the reaction that was observed when using the ethanol solvent. On the other hand, the relatively high particle size distribution in 1-hexanol yielded agglomerates.

Immobilization of Pd(OAc)2(TPPTS)2 in various renewable polysaccharides hydrogels, yielded heterogeneous catalysts that were successfully used, for the first time, in the aerobic oxidation of benzylic alcohol. The new catalysts were easily removed from the reaction mixture and recycled with some loss of activity. Among all tested polysaccharides, iota-carrageenan was found to be the most suitable support, using calcium chloride as a gelation agent.