Electrodes coated with the conducting polymer poly(3,4-ethylene dioxythiophene) (PEDOT) possess attractive electrochemical properties for stimulation or recording in the nervous system. Biomolecules, added as counter ions in electropolymerization, could further improve the biomaterial properties, eliminating the need for surfactant counter ions in the process. Such PEDOT/biomolecular composites, using heparin or hyaluronic acid, have previously been investigated electrochemically. In the present study, their biocompatibility is evaluated. An agarose overlay assay using L929 fibroblasts, and elution and direct contact tests on human neuroblastoma SH-SY5Y cells are applied to investigate cytotoxicity in vitro. PEDOT:heparin was further evaluated in vivo through polymer-coated implants in rodent cortex. No cytotoxic response was seen to any of the PEDOT materials tested. The examination of cortical tissue exposed to polymer-coated implants showed extensive glial scarring irrespective of implant material (Pt:polymer or Pt). However, quantification of immunological response, through distance measurements from implant site to closest neuron and counting of ED1+ cell density around implant, was comparable to those of platinum controls. These results indicate that PEDOT:heparin surfaces were non-cytotoxic and show no marked difference in immunological response in cortical tissue compared to pure platinum controls.

This study presents experiments designed to study the stability of the conducting polymer poly(3,4-ethylene dioxythiophene) (PEDOT), under simulated physiological conditions using phosphate-buffered saline (PBS) and hydrogen peroxide (H(2)O(2)) (0.01 M) at 37 degrees C over a 5- to 6-week period. Voltage pulsing in PBS was used as an additional test environment. The influence of switching the counter ion used in electropolymerization from polystyrene sulphonate (PSS) to heparin was investigated. Absorbance spectroscopy and cyclic voltammetry were used to evaluate the material properties. Most of the samples in H(2)O(2) lost both electroactivity and optical absorbance within the study period, but PEDOT:PSS was found slightly more stable than PEDOT:heparin. Polymers were relatively stable in PBS throughout the study period, with around 80% of electroactivity remaining after 5 weeks, disregarding delamination, which was a significant problem especially for polymer on indium tin oxide substrates. Voltage pulsing in PBS did not increase degradation. The counter ion influenced the time course of degradation in oxidizing agents.