Biomaterial-based bone grafts have an important role in the field of bone tissue engineering. One of the most promising classes of biomaterials is collagen, including the ones from marine biodiversity (in general, called spongin (SPG)). Also, hydroxyapatite (HA) has an important role in stimulating bone metabolism. Therefore, this work investigated the association of HA and SPG composites in order to evaluate their physico-chemical and morphological characteristics and their in vitro biological performance. For this, pre-set composite disks were evaluated by means of mass loss after incubation, pH, Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), and "in vitro" cell viability. pH measurements showed no statistical difference between groups. Moreover, a higher mass loss was observed for HA/SPG70/30 compared to the other groups for all experimental periods. Moreover, SEM representative micrographs showed the degradation of the samples with and without immersion. FTIR analysis demonstrated the absorption peaks for poly(methyl methacrylate) (PMMA), HA, and SPG. A higher L292 cell viability for control and PMMA was observed compared to HA and HA/SPG 90/10. Also, HA/SPG 70/30 showed higher cell viability compared to HA and HA/SPG 90/10 on days 3 and 7 days of culture. Furthermore, HA showed a significant lower MC3T3 cell viability compared to control and HA/SPG 70/30 on day 3 and no significant difference was observed between the composites in the last experimental period. Based on our investigations, it can be concluded that the mentioned composites were successfully obtained, presenting improved biological properties, especially the one mimicking the composition of bone (with 70% of HA and 30% of SPG). Consequently, these data highlight the potential of the introduction of SPG into HA to improve the performance of the graft for bone regeneration applications. Further long-term studies should be carried out to provide additional information concerning the late stages of material degradation and bone healing in the presence of HA/SPG.
Scaffolds based on aligned and non-aligned poly (L-lactic acid) (PLLA)/polycaprolactone (PCL) fibers obtained by electrospinning, associated to electrosprayed hydroxyapatite (HA) for tissue engineering applications were developed and their performance was compared in terms of their morphology and biological and mechanical behaviors. The morphological results assessed by scanning electron microscopy showed a mesh of PLLA/PCL fibers (random and perfectly aligned) associated with aggregates of nanophased HA. Fourier transform infrared spectrometry confirmed the homogeneity in the blends and the presence of nanoHA in the scaffold. As a result of fiber alignment a 15-fold increase in Young’s Modulus and an 8-fold increase in tensile strength were observed when compared to non-aligned fibers. In PLLA/PCL/HA scaffolds, the introduction of nanoHA caused a remarkable improvement of the mechanical strength of this material acting as a reinforcement, enhancing the response of these constructs to tensile stress. In vitro testing was evaluated using osteoblast (MC3T3-E1) cells. The results showed that both fibrous scaffolds were able to support osteoblast cell adhesion and proliferation and that fiber alignment induced increased cellular metabolic activity. In addition, the adhesion and proliferation of Staphylococcus aureus were evaluated and a lower number of colony forming units (CFUs) was obtained in the scaffolds with aligned fibers.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.