This study investigates the damage, microstructure, and mechanical evolution of service-exposed HP40NbTi radiant tubes of a steam reformer furnace. Tube failure was reported after 6-year of working at 525°C-830°C in the form of visible longitudinal and transverse cracks. The microstructure was evaluated using optical and scanning electron microscopy equipped with energydispersive X-ray spectrum analysis. The carbide phase transformation was determined by the method based on the matrix dissolution technique and Xray diffraction. The results of this study showed that the primary cause of the longitudinal crack formation is the local overheating and the oxidation of the dendritic grain boundaries. The M 7 C 3 carbide transforms completely into the metastable M 23 C 6 phase during high-temperature service. Metallographic examinations revealed the shrinkage cavities and creep voids that are nucleated on both Cr-and Nb-carbides. The continuous oxide layers of Cr 2 O 3 and SiO 2 formed near the inner and outer tube surfaces and the matrix's chemical composition near the outer tube surface was found to be depleted of Cr and C. Mechanical properties are irregular across the samples. A little margin of safety is noted, while the complete ductility dip is detected at room temperature. The root cause analysis of the failure under investigation showed that the tube failed due to the creep.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.