No abstract

No abstract

No abstract

Nanocellulose was successfully extracted from five different lignocellulosic biomass sources viz. banana rachis, sisal, kapok, pineapple leaf and coir using a combination of chemical treatments such as alkaline treatment, bleaching and acid hydrolysis. The shape, size and surface properties of the nanocellulose generally depend on the source and hydrolysis conditions. A comparative study of the fundamental properties of raw material, bleached and nanocellulose was carried out by means of Fourier transform infrared spectroscopy, scanning electron microscopy, atomic force microscopy, transmission electron microscopy, birefringence, X-ray diffraction, inverse gas chromatography and thermogravimetric analysis. Through the characterization of the nanocellulose obtained from different sources, the isolated nanocellulose showed an average diameter in the range of 10-25 nm, high crystallinity, high thermal stability and a great potential to be used with acid coupling agents due to a predominantly basic surface. This work provides an insight into the effective utilization of a variety of plant biomass as a potential source for nanocellulose extraction.

No abstract

No abstract

Biodegradable nanocomposite films were prepared by incorporation of cellulose nanofibrils (CNF) into alginate biopolymer using the solution casting method. The effects of CNF content (2.5, 5, 7.5, 10 and 15 wt %) on mechanical, biodegradability and swelling behavior of the nanocomposite films were determined. The results showed that the tensile modulus value of the nanocomposite films increased from 308 to 1403 MPa with increasing CNF content from 0% to 10%; however, it decreased with further increase of the filler content. Incorporation of CNF also significantly reduced the swelling percentage and water solubility of alginate-based films, with the lower values found for 10 wt % in CNF. Biodegradation studies of the films in soil confirmed that the biodegradation time of alginate/CNF films greatly depends on the CNF content. The results evidence that the stronger intermolecular interaction and molecular compatibility between alginate and CNF components was at 10 wt % in CNF alginate films.

This work presents an environmentally friendly, iodine-catalysed chemical modification method to generate highly hydrophobic, optically active cellulose nanocrystals (CNC). The high degree of ester substitution (DS=2.18), hydrophobicity, crystalline behaviour and optical activity of the generated acetylated CNC (Ac-CNC) were quantified by TEM, FTIR, solid 13C NMR, contact angle, XRD and POM analyses. Ac-CNC possessing substantial enhancement in thermal stability (16.8%) and forms thin films with interlayer distance of 50-150 nm, presenting cavities suitable for entrapping nano and micro particles. Generated Ac-CNC proved as an effective reinforcing agent in hydrophobic polymer matrices for fabricating high performance nanocomposites. When integrated at a very low weight percentage (0.5%) in an epoxy matrix, Ac-CNC provided for a 73% increase in tensile strength and a 98% increase in modulus, demonstrating its remarkable reinforcing potential and effective stress transfer behaviour. The method of modification and the unique properties of the modified CNC (hydrophobicity, crystallinity, reinforcing ability and optical activity) render them a novel bionanomaterial for a range of multipurpose applications.