We demonstrate that the simultaneous substitution of calcium and aluminum for strontium and iron in strontium hexaferrite results in a significant increase of coercivity up to a record high of 21.3 kOe. We propose that the effect is originated from a crystal structure distortion causing an increase of the magnetocrystalline anisotropy.

No abstract

The review is devoted to compounds and materials demonstrating extremely high magnetic hardness. The recent advances in the synthesis of modern materials for permanent magnets are considered, and a range of exotic compounds interesting for fundamental research is described. The key details of chemical composition, crystal structure and magnetic microstructure responsible for the appearance of high magnetic anisotropy and giant coercivity are analyzed. The challenges of developing the title materials are noted and strategies for their solution are discussed. The bibliography includes 389 references.

Magnetically hard ferrites attract considerable interest due to their ability to maintain a high coercivity of nanosized particles and therefore show promising applications as nanomagnets ranging from magnetic recording to biomedicine. Herein, we report an approach to prepare nonsintered single-domain nanoparticles of chromium-substituted hexaferrite via crystallization of glass in the system SrO–Fe2O3–Cr2O3–B2O3. We have observed a formation of plate-like hexaferrite nanoparticles with diameters changing from 20 to 190 nm depending on the annealing temperature. We demonstrated that chromium substitution led to a significant improvement of the coercivity, which varied from 334 to 732 kA m−1 for the smallest and the largest particles, respectively. The results provide a new strategy for producing high-coercivity ferrite nanomagnets.

Fe 3+ S = 5/2 ions form saw-tooth like chains along the a axis of the oxo-selenite Fe2O(SeO3)2 and an onset of long-range magnetic order is observed for temperatures below TC = 105 K. This order leads to distinct fingerprints in phonon mode linewidths and energies as resolved by Raman scattering. In addition, new excitations with small linewidths emerge below T = 150 K, and are assigned to two-magnon scattering processes with the participation of flat-band and high energy magnon branches. From this a set of exchange coupling constants is estimated. The specific ratio of the saw-tooth spine-spine and spine-vertex interactions may explain the instability of the dimer quantum ground state against an incommensurate 3D magnetic order. arXiv:1901.09617v1 [cond-mat.str-el]

A fast method for the synthesis of ε-Fe2O3, yielding 100% pure material with a variable FMR frequency, is proposed.

No abstract

No abstract