Background/purpose
Root dentin is vulnerable to acid attack, suggesting a higher risk of demineralization than coronal enamel. This study aimed to evaluate the inhibitory effect of Miswak extract on collagen degradation of demineralized dentin lesion.
Materials and methods
Demineralized bovine root dentin specimens were treated for 1 h by 20% Miswak extract and 0.12% Chlorehexidine (CHX) as a positive control group, and then subjected to collagenolytic attack (clostridium histolyticum 0.5 CDU/mL, 16 h). These cyclic treatments were repeated for 3 days. After the cyclic treatment, the images of the specimens were captured with a light microscope and the lesion depth of degraded collagen layer of all specimens was measured. The mean lesion depth was calculated and compared between the groups using descriptive and One-way ANOVA followed by Post hoc Tukey's tests. Significant level was set at p < 0.05.
Results
The mean lesion depth of CHX (28.6 ± 3.37 μm) had the least value, followed by Miswak (37.5 ± 4.01 μm) then the control (78.4 ± 18.43 μm) group. There was a significant difference in the mean lesion depth among the three groups (p = 0.000).
Conclusion
Miswak aqueous extract from
S. persica
was found to preserve the dentin collagen matrix from collagenase enzyme. This could be due to the organic compounds like flavonoids, saponins, alkaloids, tannins, and others which have been reported in literature. Present finding suggests that Miswak might play a positive effect in dentin caries prevention.
Optical coherence tomography (OCT) is an interferometric imaging technique. This study aimed to employ OCT to evaluate four different resin-based materials including a coating containing glass-ionomer filler and calcium, a giomer, and two fluoride-releasing self-etch resins. The coating and its underlying and adjacent enamel were monitored using swept-source OCT (center wavelength: 1330 nm) at baseline, after 5,000 thermal cycles, and after 1, 4 and 7 days of demineralization (pH 4.5). The coatings showed different thicknesses (60-250 micrometers) and various levels of structural and interfacial integrity. OCT could detect a demineralization inhibition zone adjacent to the edge of the fluoride-and calcium-releasing material. Localized demineralization was occasionally observed under thinner coatings. Protection of susceptible enamel surfaces by thin resin-based bioactive coatings provides protection from demineralization. OCT can be used to non-destructively monitor the integrity of such coatings, as well as enamel changes beneath and adjacent to them.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.