In this paper, lateral AlGaN/GaN Schottky barrier diodes are investigated in terms of anode construction and diode structure. An original GaN Schottky diode manufacturing-process flow was developed. A set of experiments was carried out to verify dependences between electrical parameters of the diode, such as reverse and forward currents, ON-state voltage, forward voltage and capacitance, anode-to-cathode distance, length of field plate, anode length, Schottky contact material, subanode recess depth, and epitaxial structure type. It was found that diodes of SiN/Al0.23Ga0.77N/GaN epi structure with Ni-based anodes demonstrated two orders of magnitude lower reverse currents than diodes with GaN/Al0.25Ga0.75N/GaN epitaxial structure. Diodes with Ni-based anodes demonstrated lower VON and higher IF compared with diodes with Pt-based anodes. As a result of these investigations, an optimal set of parameters was selected, providing the following electrical characteristics: VON = 0.6 (at IF = 1 mA/mm), forward voltage of the diode VF = 1.6 V (at IF = 100 mA/mm), maximum reverse voltage VR = 300 V, reverse leakage current IR = 0.04 μA/mm (at VR = −200 V), and total capacitance C = 3.6 pF/mm (at f = 1 MHz and 0 V DC bias). Obtained electrical characteristics of the lateral Schottky barrier diode demonstrate great potential for use in energy-efficient power applications, such as 5G multiband and multistandard wireless base stations.
Electrophysical characteristics and their thermal stability of thin-film resistors based on tantalum nitride (TaN) obtained by reactive magnetron sputtering were investigated. The optimal modes of the magnetron sputtering process are determined, ensuring the Ta2N phase film composition with the value of the specific electrical resistance of 250 μm cm and high thermal stability of the parameters. On the basis of the investigations carried out, thin-film matching resistors were manufactured for use as part of an electro-optical InP-based MZ modulator
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.