There is an acute need for biomaterial tools that recreate the heterogeneous brain-tumor microenvironment. A microfluidic mixing tool is reported to encapsulate glioblastoma multiforme cells within miniaturized gelatin hydrogels containing overlapping patterns of tumor-inspired matrix signals. This approach permits in situ analysis of glioma cells at the molecular and genomic level as well as the potential for clinical insight.
Objectives
To detail the development of ester-free thiol-ene dental resins with enhanced mechanical performance, limited potential for water uptake/leachables/degradation and low polymerization shrinkage stress.
Methods
Thiol-terminated oligomers were prepared via a thiol-Michael reaction and a bulky tetra-allyl monomer containing urethane linkages was synthesized. The experimental oligomers and/or monomers were photopolymerized using visible light activation. Several thiol-ene formulations were investigated and their performance ranked by comparisons of the thermo-mechanical properties, polymerization shrinkage stress, water sorption/solubility, and reactivity with respect to a control comprising a conventional BisGMA/TEGDMA dental resin.
Results
The ester-free thiol-ene formulations had significantly lower viscosities, water sorption and solubility than the BisGMA/TEGDMA control. Depending on the resin, the limiting functional conversions were equivalent to or greater than that of BisGMA/TEGDMA. At comparable conversions, lower shrinkage stress values were achieved by the thiol-ene systems. The polymerization shrinkage stress was dramatically reduced when the tetra-allyl monomer was used as the ene in ester-free thiol-ene mixtures. Although exhibiting lower Young’s modulus, flexural strength, and glass transition temperatures, the toughness values associated with thiol-ene resins were greater than that of the BisGMA/TEGDMA control. In addition, the thiol-ene polymerization resulted in highly uniform polymer networks as indicated by the narrow tan delta peak widths.
Significance
Employing the developed thiol-ene resins in dental composites will reduce shrinkage stress and moisture absorption and form tougher materials. Furthermore, their low viscosities are expected to enable higher loadings of functionalized micro/nano-scale filler particles relevant for practical dental systems.
A series of thiol-Michael and radical thiol-ene network polymers were successfully prepared from ester-free as well as ester-containing monomer formulations. Polymerization reaction rates, dynamic mechanical analysis, and solvent resistance experiments were performed and compared between compositions with varied ester loading. The incorporation of ester-free alkyl thiol, vinyl sulfone and allylic monomers significantly improved the mechanical properties when compared with commercial, mercaptopropionate-based thiol-ene or thiol-Michael networks. For polymers with no hydrolytically degradable esters, glass transition temperatures (Tg's) as high as 100 °C were achieved. Importantly, solvent resistance tests demonstrated enhanced stability of ester-free formulations over PETMP-based polymers, especially in concentrated basic solutions. Kinetic analysis showed that glassy step-growth polymers are readily formed at ambient conditions with conversions reaching 80% and higher.
Objectives
To assess the performance of thiol-ene dental composites based on selected ester-free thiol-ene formulations. Further, to point out the benefits/drawback of having a hydrolytically stable thiol-ene matrix within a glass filled composite.
Methods
Composite samples containing 50–65 wt% of functionalized glass microparticles were prepared and photopolymerized in the presence of a suitable visible light photoinitiator. Shrinkage stress measurements were conducted as a function of the irradiation time. Degrees of conversion were measured by FT-IR analysis by comparing the double bond signals before and after photopolymerization. Mechanical tests were carried out on specimens after curing as well as after extended aging in water. Dynamic mechanical analysis was employed to track the changes in storage modulus near body temperature. The properties of the thiol-ene composites were compared with those of the BisGMA/TEGDMA control.
Results
Depending on the resin type, similar or higher conversions were achieved in thiol-ene composites when compared to the dimethacrylate controls. At comparable conversions, lower shrinkage stress values were achieved. Although exhibiting lower initial elastic moduli, the thiol-ene composite’s flexural strengths were found to be comparable with the controls. Contrary to the control, the mechanical properties of the ester-free thiol-ene composites were shown to be unaffected by extensive aging in water and at least equaled that of the control after aging in water for just five weeks.
Significance
Employing non-degradable step-growth networks as organic matrices in dental composites will provide structurally uniform, tough materials with extended service time.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.