A study is reported on Langmuir and Langmuir-Blodgett (LB) films obtained by adding different percentages of stearic acid (SA) to poly(3-octylhiophene) (P3OT). Surface pressure-mean molecular area (π-A) isotherms, ultraviolet-visible (UV-Vis) absorption spectrum, atomic force microscope (AFM) and dc electrical measurements have been used for characterization. From π-A isotherms, the area per monomer for condensed films (of SA) increased according to P3OT amount. Good transfer ratios were obtained for LB deposition from P3OT/SA films with higher percentage of SA. LB films revealed linear growth as monitored by UV-Vis absorption spectra. Electrical characterization showed higher conductivity for LB film with 54 wt.% of SA. AFM images of the same film revealed high roughness and presence of large size agglomerates. Finally, interdigitated electrodes (IDE) coated with P3OT/SA LB films showed to be sensitive to the presence of volatile organic compounds.

No abstract

Low-bandgap organic polymers, poly [(4,4 bis(2 ethylhexyl)cyclopenta [2,1 b:3,4 b′]dithiophene) 2,6 diyl al (2,1,3 benzothiadiazole) 4,7 diyl](PCPDTBT), and poly [(4,4′ dioctyldithieno[3,2 b:2′,3′d] silol 2,6 diyl) alt (2,1,3 benzothiadiazole) 4,7 diyl)], (Si-PCPDTBT) were analyzed at the air-water interface forming a Langmuir monolayer. In order to form stable monolayers and to transfer to solid supports, amphiphilic molecules of stearic acid (SA) were mixed with them. For the pristine polymers, the floating monolayers were transferred onto solid substrates via the Langmuir-Schaefer (LS) technique. Surface pressure-area isotherms and compressibility modulus curves demonstrated that the SA incorporation to the polymers at the air-water interface modified the rheological properties of the Langmuir films, since the films became less compressible at higher pressures and there is clear conformational reorganization taking place at intermediary pressures. The UV-Vis absorption also depicted the changes on the overall film morphology by the shift on the maximum absorption bands, and along with cyclic voltammetry curves the absorption spectra made it possible to estimate the energy diagrams for the polymers. Photoconductivity effects were observed for all the sample, among which the pristine polymers fabricated by LS showed better results, suggesting that the organization provided by the Langmuir-Blodgett (LB) technique was not enough to overcome the insulating characteristic of the SA molecules in this specific configuration.