Mechanical polishing of glass is a time consuming process especially for lenses deviating from spherical surface such as aspheres. With laser polishing, the processing time can be significantly reduced and the wear of hard tooling can be avoided. Using laser radiation for polishing, a thin surface layer of the glass is heated up just below evaporation temperature due to the interaction of glass material and laser radiation. With increasing temperature, the reduced viscosity in the surface layer leads to the reduction of the roughness due to the surface tension. Hence, a contactless polishing method can be realized nearly without any loss of material or need of polishing agent. In this paper, results for laser polishing of fused silica, BK7, and S-TIH6 are presented with area rates up to 5 cm2/s. However, the results show that the achieved roughness with laser polishing is strongly influenced by the thermal properties of the type of glass. During laser polishing, the glass material is relocated at the surface, thus no shape errors can be corrected. To reduce the residual waviness and shape errors after laser polishing, the authors investigated a further laser-based process step (laser beam figuring, LBF) which ablates material for a shape correction. Ablation depths <5 nm allow a high precision laser ablation for selective processing. For both processes, a CO2 laser is used
Laser polishing is a technique for smoothing the surface of metallic substrates. The roughness after polishing does not only contain remains of the initial surface roughness, it also contains new roughness due to surface structures, which are introduced by the polishing process. Since these structures greatly contribute to the roughness, it is necessary to understand the mechanisms that lead to their formation so as to prevent the structures from forming and allow higher smoothing of the surface. Hence, in this publication it is investigated experimentally and numerically why these structures occur, what the influencing parameters are and how their influence on the roughness can be reduced, for both laser macro and laser micro polishing. It could be seen that the structures are influenced by the process parameters and the material of the workpiece. For a low surface roughness, the process parameters have to be adapted antithetically in some cases which means that it is not possible to prevent all structures at the same time and that surface structures will always occur during laser polishing. The process parameters must be adapted in such a way that all structures together lead to a surface roughness as low as possible.
A new approach to polish metallic freeform surfaces is polishing by means of laser radiation. In this technology a thin surface layer is molten and the surface tension leads to a material flow from the peaks to the valleys. No material is removed but reallocated while molten. As the typical processing time is 1 min/cm² laser polishing is up to 30 times faster than manual polishing. Reducing the roughness by laser polishing is achieved for several different materials such as hot work steels for the die and molding industries or titanium alloys for medical engineering. Enhancing the appearance of design surfaces is achieved by creating a dual-gloss effect by selective laser polishing (SLP). In comparison to conventional polishing processes laser polishing opens up the possibility of selective processing of small areas (< 0.1 mm²). A dual-gloss effect is based on a space-resolved change in surface roughness. In comparison to the initial surface the roughness of the laser polished surface is reduced significantly up to spatial wavelengths of 80 microns and therefore the gloss is raised considerably. The surface roughness is investigated by a spectral analysis which is achieved by a discrete convolution of the surface profile with a Gaussian loaded function. The surfaces roughness is split into discrete wavelength intervals and can be evaluated and optimized. Laser polishing is carried out by using a special tailored five-axis mechanical handling system, combined with a three axis laser scanning system and a fibre laser.
This study presents the development of post-processing steps for microfluidics fabricated with selective laser etching (SLE) in fused silica. In a first step, the SLE surface-even inner walls of microfluidic channels—can be smoothed by laser polishing. In addition, two-photon polymerization (2PP) can be used to manufacture polymer microstructures and microcomponents inside the microfluidic channels. The reduction in the surface roughness by laser polishing is a remelting process. While heating the glass surface above softening temperature, laser radiation relocates material thanks to the surface tension. With laser polishing, the RMS roughness of SLE surfaces can be reduced from 12 µm down to 3 nm for spatial wavelength λ < 400 µm. Thanks to the laser polishing, fluidic processes as well as particles in microchannels can be observed with microscopy. A manufactured microfluidic demonstrates that SLE and laser polishing can be combined successfully. By developing two-photon polymerization (2PP) processing in microchannels we aim to enable new applications with sophisticated 3D structures inside the microchannel. With 2PP, lenses with a diameter of 50 µm are processed with a form accuracy rms of 70 nm. In addition, this study demonstrates that 3D structures can be fabricated inside the microchannels manufactured with SLE. Thanks to the combination of SLE, laser polishing and 2PP, research is pioneering new applications for microfluidics made of fused silica
Surface structuring by remelting with laser radiation is a new approach to shape metallic surfaces ("WaveShape"). In this structuring process, surface material is reallocated in its molten state instead of being removed, because the process is based on the new active principle of remelting. The surface structure and the microroughness result from a laser-controlled melt pool due to surface tension. Basic research has been conducted with promising results, especially for the hot work steel 1.2343. Since remelting is a thermally driven process, significant differences between metallic materials were expected due to their thermophysical properties such as thermal conductivity, absorption coefficient, viscosity, heat capacity, etc. Therefore, the presented research soughed to expand the spectrum of processable materials. Within the framework of our investigation, we compared the achieved structure height as well as melt pool dimensions for six different materials. Furthermo re, we successfully tested new structuring strategies such as not linearly shaped scanning vectors to create innovative surface structures on all materials investigated. The biggest structures were achieved on the titanium alloy Ti6Al4V and the nickel based super alloy IN718. Finally, an approach of reverse structuring was investigated in order to erase existing structures and achieve a smoothed rewriteable metallic surface. The results show that surface structuring by laser remelting is well suited to process a wide range of different metals and to achieve a broad variety of different structures as well as to effectively erase existing surface structures such as milling marks
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.