Shot-peened titanium alloy Ti-6Al-4V and nickel-based super alloy IN100 were subjected to plain and fretting fatigue under cylinder-on-flat contact condition at room temperature. Measurement of compressive residual surface stress from shot-peening before and after fretting showed relaxation, which was significant in IN100 and near the contact surface. The fretting fatigue life of IN100 did not improve significantly due to shot-peening, while there was considerable improvement for Ti-6Al-4V and relatively less relaxation of the residual surface stress. Further, fretting had a relatively more detrimental effect on the fatigue performance of Ti-6Al-4V than in the case of IN100. A critical plane-based fatigue crack initiation model, a modified shear stress range parameter, was computed from finite element analysis for two levels of residual surface stress relaxation: no relaxation and complete relaxation. This analysis suggested that not only crack initiation but also propagation should be considered to characterize fretting fatigue behavior of shot-peened specimens; however, it showed an appropriate trend with the measured fretting fatigue life and agreement with several other experimental observations.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.