Filler flocculation was followed for silica filled compounds containing various alkoxy silanes and non-silane type polar additives. The methodology employed in this paper permitted a quantitative characterization of filler flocculation and polymer-filler interactions after heating the compound under conditions that simulated vulcanization. With the addition of trialkoxy silanes, the reduction of filler flocculation and the degree of polymer-filler interactions were found to depend on the type and the concentration of silane added, and on the mixing drop temperature (Td) used. Greater polymer-filler interactions and flocculation suppression were obtained with a compound containing a tetrasulfane when compared to that containing either a disulfane or a monofunctional-silane. Polar additives such as an amine compound and a sugar alcohol did not reduce the silica flocculation during simulated vulcanization because they were dewetted from the silica surface upon heating. The filler flocculation process was monitored by following the change of dynamic storage moduli using an on-line rheometer. The flocculation process order and process constant were extracted from the non-linear regression analysis of the kinetic data. These kinetic parameters were used to quantify the suppression of filler flocculation by the additives used. Filler flocculation was found not to be affected by the vulcanization process because it occurred prior to the onset of cure.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.