Oligochitosans (OCT) were prepared from chitosan (CTS) by gamma irradiationtechnique. The parameters affecting to the chitosan degradation were studied. And then, OCT nanoparticles wereformed using the method of tripolyphosphate (TPP) cross-linking. Effect of concentration and molecular weight of OCT, concentration of TPP on particle size of the formed OCT nanoparticles were also studied. The formation of OCT nanoparticles was verified by Fourier transform infrared (FT-IR) spectrometer and differential scanning calorimeter (DSC), the morphology was observed using scanning electron microscope (SEM), and the characteristics (particle size and zeta potential) of OCT nanoparticles were also studied. The effect of OCT nanoparticles on strawberry presevation was carried out using the coating method. Results showed that an increase in radiation dose resulted in a decrease of chitosan molecular weight. The OCT with molecular weight of approximately 7.7 kDa was obtained by the synergistic effect of hydrogen peroxide (5 %, v/v) and gamma ray at dose of 30 kGy. The smaller OCT nanoparticles was obtained with a lower molecular weight of OCT. The results of FTIR, DSC indicated the success in the formation of OCT nanoparticles with the particle size approximately 129.9 nm, with the spherical shape. The application of OCT nanoparticles on strawberry has prolonged the preservation times approximately 2.5 times higher comp
Silver nanoparticles were prepared from (Ag+) aqueous solution by the method of γ-ray irradiation using chitosan as stabilizer. The saturated conversion dose (Ag+ à Ago) determined by UV-Vis spectroscopy was found to be about 16 kGy. The UV-Vis spectrum showed that an absorption peak at λmax = 400 nm due to surface plasma resonance. The image of transmission electron microscopy (TEM) showed that the silver nanoparticles were mostly spherical in shape and the average diameter was of about ~ 12 nm. The prepared colloidal silver nanoparticles solution was in good stability during storage time.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.