The purpose of the study was to determine the wear rate of Equia Forte HT Fil with Equia Forte Coat or without coating and compare it with Fuji IX GP high-viscosity glass ionomer cement (GIC) in conditions with acid load or at neutral pH. The samples were stored for 7 days: (1) in artificial saliva, (2) in artificial saliva and cyclically exposed to low pH, and (3) in distilled water and cyclically exposed to low pH. Wear was determined by measuring the difference in mass before and after brushing in an abrasion testing device. The wear of Fuji IX GP was significantly higher than that of Equia Forte HT Fil with or without coating (p = 0.000). The difference between Equia Forte HT Fil with and without Coat was not statistically significant (p < 0.803). The differences in wear resistance between samples stored in saliva and in distilled water were not significant (p = 0.588). Periodic exposure to the low pH solution significantly affected the wear resistance of all materials (p = 0.000). Equia Forte HT Fil was more resistant to wear than Fuji IX GP in all storage conditions. A resinous coat did not significantly increase wear resistance.

This study investigates the morphology, composition and corrosion resistance of hot dip galvanized (HDG) steel bolts in fresh water, 1% NaCl saltwater in the presence of protective compounds L-Tryptophan and three conventional corrosion inhibitors: Inhibitor 1-VCI (amine-carboxylates-based), Inhibitor 2 (based on carboxylate acid), and Inhibitor 3 (water-based, carboxylate acid). Quantitative tests performed include gravimetric analysis and electrochemical techniques, such as linear polarization, Tafel extrapolation, and Electrochemical Impedance Spectroscopy (EIS). Electrochemical measurements determined the polarization resistance Rp, corrosion rate vcorr, and corrosion potential Ecorr. Furthermore, Scanning Electron Microscopy (SEM) and ATR-FTIR spectrometry were used to evaluate and characterize the formed layers on the surface of hot-dip galvanized steel samples. The results reveal that upon corrosion new compounds are formed onto the exposed areas of the treated bolts such as zinc-carbonates, zinc-hydroxides, etc. The presence of these compounds on the surface of the HDG steel bolts hinders the corrosion process by reducing the rate of the anodic and cathodic reactions. The gravimetric test showed that L-tryptophan in distilled water has mass increase, resulting from the formation of white deposits on the sample surface. In fresh water and distilled water, the best corrosion resistance was achieved with Inhibitor 1-VCI, while L-tryptophan showed best results in 1% NaCl solution.

Laser surface texturing is a technology that enables us to achieve very complex surface geometries. In this study, geometries created on the Ti-6Al-4V surface were in the form of parallel grooves. Those geometries were obtained by changing the laser beam speed and the number of passes (one or two). The effects of laser texturing on the roughness and the contact angle of Ti-6Al-4V surfaces on the first day and after 80 days were investigated. The results of this study indicate that the samples treated with two passes of the laser beam and at a lower speed scan show regularities of roughness profile geometry while other laser-treated samples do not. It is shown that the surfaces laser-textured with either one or two passes of the laser beam show no significant changes in the surface wettability after 80 days. The statistical test proves that there is a significant difference (level α = 0.05) between the contact angles on the untreated sample on the first day and after 80 days of treatment.