In this work the surface tension of poly(vinyl butyral) was evaluated for temperatures ranging from 240 to 260 °C, using the pendant drop method. The surface tension values obtained were in the same range as the ones obtained for other molten polymers; However the variation of surface tension with temperature was more than ten times larger than for other molten polymers. This difference was attributed to a chemical change of the polymer during the surface tension measurement.
SÃOEscola Politécnica da USP tem sido estudadas blendas de Poliamida-6 (PA-6) e filme de poli(vinil butiral) (PVB), como uma alternativa para reciclagem do filme de PVB oriundo do processo de separação dos componentes do vidro laminado pós-consumo.As propriedades mecânicas de uma blenda polimérica dependem da sua morfologia e, por sua vez, a morfologia depende das propriedades reológicas e da tensão interfacial entre os polímeros formadores da blenda, que para o caso de blendas envolvendo filme de PVB podem mudar em função da concentração de plastificante presente na composição do filme. Apesar da importância do seu conhecimento, a tensão interfacial entre PA-6 e filme de PVB não é conhecida. O presente trabalho teve como objetivo avaliar a tensão superficial do filme de PVB e da PA-6. O método utilizado foi o da gota pendente. Também estudou-se a influência da adição de plastificante na tensão superficial do filme de PVB. Os resultados mostraram que a tensão superficial dos polímeros estudados decresce com o aumento da temperatura (temperatura variando entre 240 e 260ºC). Em particular, para o filme de PVB a entropia de superfície (-(dγ/dT) ) apresentou um valor acima dos normalmente encontrados para polímeros fundidos. Este comportamento foi atribuído à estabilidade térmica do filme. O filme de PVB utilizado nos ensaios de tensão superficial foi caracterizado por Espectroscopia no Infravermelho (FTIR), Espectroscopia no Ultravioleta/Visível (UV-VIS), EspectroscopiaEletrônica para Análise Química (ESCA) e Análise Termogravimétrica (TG). Os resultados obtidos comprovaram que há mudanças na estrutura do PVB durante sua exposição a temperaturas elevadas, por longo período de tempo (condições do ensaio de tensão superficial). Foi observado, primeiramente, a evaporação do plastificante, seguida por perda de grupos polares (-OH, C=O e C-O-C) presentes na estrutura do PVB. A tensão superficial da Poliamida-6 foi determinada para temperaturas de 250 e 260ºC. Os resultados mostraram que a PA-6 manteve-se estável durante os ensaios. However, to our knowledge neither the PA-6/PVB film interfacial tension nor the surface tension of PVB film at temperatures above softening temperatures have been evaluated.In this work, the surface tension of poly(vinyl butyral) and polyamide was evaluated using the pendant drop method. Also it was tried to evaluate the surface tension of PVB film as a function of plasticizer content. The surface tension values obtained were in the same range as the ones obtained for other molten polymers: the surface tension decreases with increasing temperature (for temperatures ranging from 240 to 260°C).However, the value of PVB film surface entropy (-(dγ/dT) where γ is the surface tension and T is the temperature) was much larger than values reported for other molten polymers. This result was attributed to thermal stability of PVB film during the surface tension measurement. The drops of PVB film after surface tension analysis were examined for any change in their functional groups using infrared spectr...
In this work, the effect of the incorporation of a sodium smectite clay (Brasgel) in Nylon-6 toughened with Poly (vinyl butyral) film (PVB film) was evaluated. The composites contain 60 wt.% of Nylon-6, 40 wt.% of PVB film and 5 wt.% of clay, relative to the total weight of the mixture. The clay was previously purified by sedimentation, and dried in a spray-dryer at 150°C. The composites were obtained by extrusion, in two steps: step 1 - mixture of nylon-6 with clay (called master of nylon-6) and step 2 - mixture of master of nylon-6 with PVB film. The clay was characterized by X-ray diffraction and X-rayfluorescence. The composites were characterized by mechanical tests (tensile and notched Izod impact strength), X-ray diffraction and scanning electron microscopy (SEM). The composites showed significant increase in the values of the notched Izod impact strength, when compared to the ones for pure nylon-6, and kept the stiffness of the matrix phase.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.