Produced via electrospinning, polyurethane membrane, which has a unique property, has been of interest in medical fields. Electrospinning is a process by which nanofibers can be produced by an electrostatically driven jet of polymer solution. Electrospun fibers are collected in the form of membranes. The porous structured electrospun membrane is particularly important for its favorable properties: it exudates fluid from the wound, does not build up under the covering, and does not cause wound desiccation. The electrospun nanofibrous membrane shows controlled evaporative water loss, excellent oxygen permeability, and promoted fluid drainage ability, but still it can inhibit exogenous microorganism invasion because its pores are ultra-fine. Histological examination indicates that the rate of epithelialization is increased and the dermis becomes well organized if wounds are covered with electrospun nanofibrous membrane. This electrospun membrane has potential applications for wound dressing based upon its unique properties.

Summary: An electrospun nonwoven fabric of a cationic polysaccharide, chitosan, was successfully prepared. The present study focuses on the effect of the electrospinning solvent and the chitosan concentration on the morphology of the resulting nonwoven fabrics. The solvents tested were dilute hydrochloric acid, acetic acid, neat formic acid and trifluoroacetic acid. As the chitosan concentration was increased, the morphology of the deposition on the collector changed from spherical beads to interconnected fibrous networks. The addition of dichloromethane to the chitosan‐TFA solution improved the homogeneity of the electrospun chitosan fiber. Under optimized conditions, homogenous (not interconnected) chitosan fibers with a mean diameter of 330 nm were prepared.Effects of the coexisting dichloromethane (MC) in the prespun chitosan‐TFA solution on the morphology of the electrospun chitosan fibers. The volume ratio of TFA:MC was 70:30 (×5 000).magnified imageEffects of the coexisting dichloromethane (MC) in the prespun chitosan‐TFA solution on the morphology of the electrospun chitosan fibers. The volume ratio of TFA:MC was 70:30 (×5 000).

No abstract