Fe/Mo single doped and codoped TiO 2 thin films were spin coated on polished fused silica substrates and annealed in air at 450 °C for 2 h. The XPS data for the anatase thin films were distinctive in showing that Fe-doping caused Ti 4+ reduction, Mo-doping caused Ti 4+ oxidation, and codoping did not alter the Ti valence. The XPS data also showed that the precursor valences of Fe 3+ and Mo 5+ were reduced upon annealing. Analysis of the potential roles of thermodynamics and intervalence charge transfer (IVCT) demonstrates that the latter drives the equilibria both in solution and during annealing. Photocatalytic performance testing indicated that Fe-doping was slightly deleterious, Mo doping had a consistent positive effect, and codoping exhibited a clear negative trend as a function of doping concentration. These results are interpreted in terms of the effect of IVCT on the matrix valence, dopant valences, and charge carrier trapping. Fe doping exhibited reduced performance because both matrix Ti (4−x)+ and dopant Fe (3−y)+ acted as electron traps. Mo doping exhibited enhanced performance because the matrix Ti (4+x)+ acted as a hole trap and the dopant Mo (5−x)+ and Mo (4−x)+ acted as electron traps, thereby promoting charge separation. Codoping exhibited a clearly detected negative trend on the performance because, while Ti 4+ played no role, Fe (3−y)+ , Mo (5−x)+ , and Mo (4−x)+ all acted as traps for the majority charge carrier electrons.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.