A new structural fluorine-containing methacrylate monomer CH2=C(CH3)COOC–(CF3)2CF2CF2CF3 (5) was synthesized derived from perfluoro-2-methyl-2-pentene (D2). A homopolymer of 5 and copolymers of 5 and methacrylate with different alkyl chain length (chain length n = 1, 2, 4, 6, 8, 12, 18) were obtained. These new fluorinated acrylate polymers showed excellent water and oil repellency. The contact angle of the films of the homopolymer and part of the copolymers were similar with the corresponding polymers prepared from CH2=CHC(O)OCH(C3F7)(CF(CF3)2), but greater than that of the C6F13(CF3)CHOC(O)CH=CH2 homopolymer. The structure-property relationship research indicated that the copolymers’ hydrophobicity decreased first and then increased with the increase of alkyl chain length. Td of all the polymers were greater than 220 °C and Tg fluctuated within the range of −51~103.8 °C. Contact angle and Tg could be adjusted by controlling the feed ratio of monomer to meet the requirements of technical indicators in the practical applications. The outstanding liquid repellency and thermal stability make monomer 5 a promising alternative to perfluorinated long-chain fluorosurfactants.
Fluorocarbon surfactants were the main components of aqueous film-forming foam extinguishing agents (AFFF). Unfortunately, the widely used fluorocarbon surfactant perfluorooctane sulfonate (PFOS) was limited due to its toxicity, bioaccumulation and biodegradability. In this paper, an environmentally friendly quaternary ammonium cationic fluorocarbon surfactant with high surface activity and simple synthesis route was reported. The surface performance and aggregation behavior of the mixed solution of this fluorocarbon surfactant and sodium n-octyl sulfate were studied by means of surface tension meter and transmission electron microscope (TEM). The results showed that the synergistic effect of sodium n-octyl sulfate and this fluorocarbon surfactant was significant, and many vesicles could be observed in the mixed solution with the concentration of 0.1 mol/L under TEM. Subsequently, three environmental friendly AFFF formulations (F-1, F-2, F-3) were designed with the mixture of the fluorocarbon surfactant, sodium n-octyl sulfate and lauryl betaine BS-12 as foaming agent. Through its foam performance test, it could be seen that F-3 showed relatively excellent foam performance. The initial foam height h 0 was 70 mm, the 25% drainage time was 315 s, the extinguishing time was 28 s, and the burn-back time was 720 s. This kind of fire extinguishing agent had the potential of fire protection application.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.