It is well stablished that heating efficiency of magnetic nanoparticles under radiofrequency fields is due to the hysteresis power losses. In the case of microwires (MWs), it is not clear at all since they undergo non-coherent reversal mechanisms that decrease the coercive field and, consequently, the heating efficiency should be much smaller than the nanoparticles. However, colossal heating efficiency has been observed in MWs with values ranging from 1000 to 2800 W/g, depending on length and number of microwires, at field as low as H = 36 Oe at f = 625 kHz. It is inferred that this colossal heating is due to the Joule effect originated by the eddy currents induced by the induction field B = M + χH parallel to longitudinal axis. This effect is observed in MWs with nearly zero magnetostrictive constant as Fe2.25Co72.75Si10B15 of 30 μm magnetic diameter and 5 mm length, a length for which the inner core domain of the MWs becomes axial. This colossal heating is reached with only 24 W of power supplied making these MWs very promising for inductive heating applications at a very low energy cost.
Co-based amorphous microwires presenting the giant magnetoimpedance effect are proposed as sensing elements for high sensitivity biosensors. In this work we report an experimental method for contactless detection of stress, temperature, and liquid concentration with application in medical sensors using the giant magnetoimpedance effect on microwires in the GHz range. The method is based on the scattering of electromagnetic microwaves by FeCoSiB amorphous metallic microwires. A modulation of the scattering parameter is achieved by applying a magnetic bias field that tunes the magnetic permeability of the ferromagnetic microwires. We demonstrate that the OFF/ON switching of the bias activates or cancels the amorphous ferromagnetic microwires (AFMW) antenna behavior. We show the advantages of measuring the performing time dependent frequency sweeps. In this case, the AC-bias modulation of the scattering coefficient versus frequency may be clearly appreciated. Furthermore, this modulation is enhanced by using arrays of microwires with an increasing number of individual microwires according to the antenna radiation theory. Transmission spectra show significant changes in the range of 3 dB for a relatively weak magnetic field of 15 Oe. A demonstration of the possibilities of the method for biomedical applications is shown by means of wireless temperature detector from 0 to 100 °C.
The following work addresses new configurations of sensing array platforms that are composed of Co-based amorphous ferromagnetic microwires (MWs) to obtain an enhanced modulation of the microwave scattering effects through the application of low strength DC or AC magnetic fields. An amorphous MW is an ultrasoft ferromagnetic material (coercivity ~0.2 Oe) with a circumferential magnetic anisotropy that provides a high surface sensitivity when it is subjected to an external magnetic field. Firstly, microwave scattering experiments are performed as a function of the length and number of MWs placed parallel to each other forming an array. Subsequently, three array configurations are designed, achieving high S21 scattering coefficients up to about −50 dB. The influence of DC and AC magnetic fields on S21 has been analyzed in frequency and time domains representation, respectively. In addition, the MWs sensing array has been overlapped by polymeric surfaces and the variations of their micrometric thicknesses also cause strong changes in the S21 amplitude with displacements in the frequency that are associated to the maximum scattering behavior. Finally, a new concept for amplifying microwave scattering is provided by intercalating Cu MWs into the linear Co-based arrays. The designed mixed system that is composed by Co-based and Cu MWs exhibits a higher S21 coefficient when compared to a single Co-based MW system because of higher electrical conductivity of Cu. However, the ability to modulate the resulting electromagnetic scattering is conferred by the giant magneto-impedance (GMI) effects coming from properties of the ultrasoft amorphous MWs. The mixed array platform covers a wide range of sensor applications, demonstrating the feasibility of tuning the S21 amplitude over a wide scattering range by applying AC or DC magnetic fields and tuning the resonant frequency position according to the polymeric slab thickness.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.