Cobalt sulfide thin films were synthesized from acidic chemical baths by varying the deposition time. The powder X-ray diffraction studies indicated that there are hexagonal CoS, face-centered cubic Co3S4, and cubic Co9S8 phases of cobalt sulfide. The crystallite size of the hexagonal CoS phase decreased from 52.8 nm to 22.5 nm and that of the cubic Co9S8 phase increased from 11 nm to 60 nm as the deposition time increased from 2 hrs to 3.5 hrs. The scanning electron microscopic images revealed crack and pinhole free thin films with uniform and smooth background and few large polygonal grains on the surface. The band gap of the cobalt sulfide thin films decreased from 1.75 eV to 1.3 eV as the deposition time increased from 2 hrs to 3.5 hrs. The photoluminescence (PL) spectra of the films confirmed the emission of ultraviolet, violet, and blue lights. The intense PL emission of violet light at 384 nm had red shifted with increasing deposition time that could be resulted from the increase in the average crystallite size. The FTIR spectra of the films indicated the presence of OH, C-O-H, C-O, double sulfide, and Co-S groups. As the deposition time increased, the electrical resistivity of the cobalt sulfide thin films decreased due to the increase in both the crystallite size and the films’ thickness.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.