In this study, electroless nickel plating and electrodeposition were used to deposit thin films on the polymer lattice template prepared by 3D printing, then seven Octet hollow nickel lattice materials with different structural parameters were synthesized by etching process at the expense of the polymer backbone. The microstructure and properties of the Octet structure nickel lattice were characterized by X-ray diffraction, Electron backscattering diffraction and transmission electron microscopy. According to the results, the average grain size of the electrodeposition Ni lattice material was 429 nm, and (001) weak texture was found along the direction of the film deposition. The lattice deformation mode changed with the increase of the lattice length-to-diameter ratio, and it shifted from the lattice deformation layer-by-layer and the overall deformation to the shear deformation in the 45° direction. The strength, modulus and energy absorption properties of the Octet lattice increased with the density, and they were exponentially related to density. In the relative density range of 0.7~5%, Octet hollow Ni lattices with the same density conditions but different structural parameters showed similar compressive strength and elasticity modulus; the energy absorption capacity, however, was weakened as the length-to-diameter ratio increased.

NiCr alloys with different components were obtained by pack chromation and homogenization heat treatment of octet Ni lattice. The microstructure, alloy composition, microhardness and quasi-static compression properties of the NiCr lattice were tested. The results showed that after homogenization heat treatment, the NiCr alloy lattice had an austenitic structure with uniform composition. Compared with the pure nickel lattice, the microhardness, compressive strength, elastic modulus and energy absorption of the NiCr lattice increased with the increase of chromium content. The microhardness, specific strength, specific modulus and specific energy absorption of the Ni-45Cr alloy were 363 HV, 11.1 MP/(g/cm3), 1169.1 MP/(g/cm3) and 10 J/g, respectively, which were attributed to the solid solution strengthening provided by chromium and the increase in density. NiCr alloy lattices have high strength and toughness and may have potential applications in high-temperature filters or heat exchangers.