The present research demonstrates the synthesis and characterization of LaMnO3 perovskite powders using the sol-gel technique for dye-sensitive solar cell applications. With this respect, transparent solutions were prepared from La and Mn based precursors, distilled water and citric acid monohydrate. Ammonium hydroxide was incorporated into the La-Mn solution in order to neutralize/precipitate at 24oC for 1 hour in the air. The solution was allowed to evaporate on a hot plate device at 90 °C in the air. The obtained solutions were dried at 90 oC for 24 hours to form a xerogel structure, dried at 200 oC for 2 hours and consequently annealed at 500 and 850 oC for 2 hours in the air. Thermal, structural, microstructural, optical and magnetic properties of the powders were characterized through differential thermal analysis-thermogravimetry (DTA-TG), Fourier transform infrared (FTIR), X-ray diffraction (XRD), X-ray Photoelectron Spectroscopy (XPS), scanning electron microscopy (SEM), Malvern zeta sizer (PSD), UV-vis spectrometer and vibrating sample magnetometer (VSM). The obtained results indicate promise, especially the low band range, that LaMnO3 powders can be used in dye-sensitized solar cells and can positively affect performance and efficiency.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.