51CrV4 steel is extensively used in large-size damping springs for trains and vehicles. Quenching conditions play an important role in performance enhancement. The present work investigated the effects of various oil-bath temperatures and out-of-oil temperatures on the microstructure and the mechanical properties of this steel. The morphological examination focused on both the quenched martensite and the tempered troostite. Tensile and hardness tests were carried out to evaluate the mechanical properties. The results showed that a coarsening of the martensite occurred at a high oil-bath temperature. In addition, the size and fraction of bainite islands also increased with the increase of oil-bath temperature. In contrast, the carbide size and the intercarbide spacing both increased with the increase of oil-bath temperature. Thus, the tensile strength and the hardness both decreased with increasing oil-bath temperature in accordance with the Hall-Petch relationship. Correspondingly, the ductility increased as the oil-bath temperature increased. At a relatively high out-of-oil temperature, the martensite underwent an auto-tempering process, which led to the precipitation of many tiny carbide particles in the as-quenched martensite laths. This auto-tempering effect enhanced the width of large-sized carbides and reduced their length in the final microstructure. The intercarbide spacings increased with increasing out-of-oil temperature. As the oil-bath temperature increased, the tensile strength and hardness decreased, and the ductility increased. The fracture morphology was examined to explain the results of mechanical properties.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.