To investigate the impact of radiotherapy on surface properties of restorative dental materials. A conventional resin composite—CRC (Aura Enamel), a bulk-fill resin composite—BFRC (Aura Bulk-fill), a conventional glass ionomer cement—CGIC (Riva self cure), and a resin-modified glass ionomer cement—RMGIC (Riva light cure) were tested. Forty disc-shaped samples from each material (8 mm diameter × 2 mm thickness) (n = 10) were produced according to manufacturer directions and then stored in water distilled for 24 h. Surface wettability (water contact angle), Vickers microhardness, and micromorphology through scanning electron microscopy (SEM) before and after exposition to ionizing radiation (60 Gy) were obtained. The data were statistically evaluated using the two-way ANOVA and Tukey posthoc test (p < 0.05). Baseline and post-radiation values of contact angles were statistically similar for CRC, BFRC, and RMGIC, whilst post-radiation values of contact angles were statistically lower than baseline ones for CGIC. Exposition to ionizing radiation statistically increased the microhardness of CRC, and statistically decreased the microhardness of CGIC. The surface micromorphology of all materials was changed post-radiation. Exposure to ionizing radiation negatively affected the conventional glass ionomer tested, while did not alter or improved surface properties testing of the resin composites and the resin-modified glass ionomer cement tested.
ResumoIntrodução: Os cimentos de ionômero de vidro possuem limitações devido à sua baixa resistência mecânica, a qual está diretamente relacionada com a proporção pó/líquido e a sua manipulação. Com o intuito de padronizar o proporcionamento e a manipulação, surgiram os cimentos de ionômero de vidro encapsulados, os quais possuem proporção pré-estabelecida e manipulação mecânica. Objetivo: Comparar, in vitro, a resistência ao desgaste entre os cimentos de ionômero de vidro pó/líquido (Riva self cure e Riva light cure) e os encapsulados (Riva self cure e Riva light cure). Material e método: As amostras foram divididas em quatro grupos, tendo sido confeccionados 48 corpos de prova (n=12), sendo 12 para cada grupo, com as seguintes dimensões: 7 mm de diâmetro e 4 mm de espessura. O desgaste foi avaliado de acordo com a massa perdida no processo de escovação (10.000 ciclos). Os valores obtidos na diferença entre a massa inicial e a massa final foram submetidos à análise de variância ANOVA e Teste de Tamhane (p<0,05). Resultado: Segundo os resultados obtidos, todas as amostras sofreram perda de massa estatisticamente significativa e, em ordem crescente de desgaste, temos os cimentos de ionômero de vidro modificado por resina -para os quais não houve diferença significativa entre o sistema pó/líquido (ΔM=11,62 mg e p=0,001) e o encapsulado (ΔM=12,96 mg e p=0,003) (p>0,05) -seguidos pelo convencional pó/líquido (ΔM=20,68 mg e p=0,014) e o convencional encapsulado (ΔM=47,95 mg e p=0,002). Conclusão: Pode-se conseguir uma resistência ao desgaste semelhante e até melhor no sistema pó/líquido. Descritores: Cimentos de ionômero de vidro; resistência; desgaste. AbstractIntroduction: The glass ionomer cements presents limitations because of their low mechanical strength, which is directly related to the powder / liquid proportion and handling. Aiming to standardize the proportioning and handling, first came the encapsulated glass ionomer cements, which have pre-determined ratio and mechanical manipulation. Objective: To compare the in vitro wear resistance of the encapsulated glass ionomer cements (Riva Self Cure and Riva Light Cure) and powder/liquid (Riva Self Cure and Riva Light Cure). Material and method: The samples were divided into four groups which were made 48 specimens (n=12), 12 for each group with 7 mm diameter by 4 mm thick, and the wear was evaluated according to the mass lost in the process of brushing (10,000 cycles). The obtained values on the difference of the initial and final mass were analyzed using ANOVA and Tamhane's test (p<0.05). Result: Resulting found that all groups had loss of statistically significant mass, and in ascending order of wear have the light-cured glass, which there was no statistically significant differences between the powder /liquid ionomer (ΔM=11,62mg p=0.001) and encapsulated (ΔM=12,96mg p=0.003) (p<0,05), followed by conventional self-curing (ΔM=20,68mg p=0.014) and encapsulated self-curing (ΔM=47,95mg p=0.002). Conclusion: Conclude that despite the glass ionomer cement encapsul...
Introdução: uma polimerização adequada é crucial para a obtenção das propriedades físicas ideais e o desempenho clínico das resinas compostas. Objetivo: avaliar o grau de conversão (GC) e dureza de resinas IntroduçãoDesenvolvidas por Bowen durante a década de 1960, as resinas compostas à base de BisGMA passaram por transformações com o intuito de melhorar suas propriedades mecânicas e estéticas 1 . Concomitantemente à evolução desses materiais, os pacientes buscam cada vez mais a excelência estética ao sorrir, o que leva ao desenvolvimento de resinas que, além de devolver a forma e função do dente, favoreçam a harmonia do sorriso de maneira natural. Sendo assim, por proporcionar ao profissional a capacidade de restabelecer a estética do sorriso, confeccionar restaurações em dentes posteriores, além do seu baixo custo, quando comparadas
Introdução: Os sistemas adesivos possibilitam a execução de restaurações estéticas e minimamente invasivas, sendo, portanto, objeto de pesquisas para contornar os problemas que se apresentam no procedimento restaurador. Objetivo: Avaliar in vitro a resistência de união de um sistema adesivo autocondicionante, e deste modificado com soluções extrativas de semente de uva. Metodologia: Duas soluções extrativas foram preparadas com extrato de semente de uva em pó dissolvido em acetona e etanol. A partir delas e de um adesivo, seis sistemas adesivos autocondicionantes experimentais foram preparados, diferindo quanto ao solvente utilizado e às proporções entre adesivo puro e solução extrativa, esta, variando em 7,5%, 15% e 30%. Setenta incisivos bovinos hígidos tiveram as raízes removidas com disco de carborundum e as faces vestibulares desgastadas com lixas d’água de granulação 120, 240, 600 e 1200 sob refrigeração até expor a dentina superficial. Os dentes foram distribuídos aleatoriamente em sete grupos distintos: Controle; A7,5; A15; A30; E7,5; E15; e E30, contendo 10 elementos cada. A aplicação dos adesivos foi executada de acordo com as recomendações do fabricante do adesivo controle. A restauração foi realizada com uma matriz de silicone com dimensões 2 mm de altura e 4 mm de diâmetro e inserido o material restaurador em incremento único e fotopolimerizado por 40s. Após três meses armazenados em água destilada, os espécimes foram submetidos ao teste de resistência de união. Foi empregado o método estatístico Teste Paramétrico Anova 1 Fator e pós- teste de Tamhane (p<0,05). Resultados: Os grupos A7,5, E7,5 e E30 não apresentaram diferença em relação ao grupo Controle; A15 e A30 mostraram desempenho estatisticamente semelhante entre si; e E15 não apresentou diferença estatística em relação aos outros adesivos. Conclusões: A adição de proantocianidina teve efeitos diferentes, dependendo dos solventes e das concentrações utilizadas, mas sem alterar significativamente o desempenho do adesivo.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.