Monowave and polywave LEDs emitted nonhomogeneous light beams, but this did not affect the DC homogeneity of bulk fill composites. For composites containing CQ associated with alternative photoinitiators, polywave LEDs had a higher DC, but only at the top part of the restoration; lower wavelength absorption photoinitiators were ineffective in deeper areas.
Establishing the efficacy of different artificial aging methods and differences between color change using CIELAB and CIEDE2000 formulas are important to standardize color stability evaluations and facilitate the comparison of outcomes from different studies in the literature.
The long-term color stability of composite restorations is a critical aspect of esthetic restorative procedures. Optimal Polymerization behavior of resin composite as indicated by the degree of conversion also influence on the color stability after artificial aging of composite restorations.
The increase in filler particle loading negatively affected monomer conversion and color stability of resin-based composites. As reduced filler loading results in poorer mechanical properties, to enhance color stability, resin-based composites should be formulated by making the refractive index of the polymeric matrix more closely match that of the filler throughout the polymerization process. (J Esthet Restor Dent, 2016).
The aim of this study was to evaluate the degree of conversion (DC) and the cytotoxicity of photo-cured experimental resin composites containing 4-(N,N-dimethylamino)phenethyl alcohol (DMPOH) combined to the camphorquinone (CQ) compared with ethylamine benzoate (EDAB). The resin composites were mechanically blended using 35 wt% of an organic matrix and 65 wt% of filler loading. To this matrix was added 0.2 wt% of CQ and 0.2 wt% of one of the reducing agents tested. 5x1 mm samples (n=5) were previously submitted to DC measurement and then pre-immersed in complete culture medium without 10% (v/v) bovine serum for 1 h or 24 h at 37 °C in a humidifier incubator with 5% CO2 and 95% humidity to evaluate the cytotoxic effects of experimental resin composites using the MTT assay on immortalized human keratinocytes cells. As a result of absence of normal distribution, the statistical analysis was performed using the nonparametric Kruskal-Wallis to evaluate the cytotoxicity and one-way analysis of variance to evaluate the DC. For multiple comparisons, cytotoxicity statistical analyses were submitted to Student-Newman-Keuls and DC analysis to Tukey's HSD post-hoc test (=0.05). No significant differences were found between the DC of DMPOH (49.9%) and EDAB (50.7%). 1 h outcomes showed no significant difference of the cell viability between EDAB (99.26%), DMPOH (94.85%) and the control group (100%). After 24 h no significant difference were found between EDAB (48.44%) and DMPOH (38.06%), but significant difference was found compared with the control group (p>0.05). DMPOH presented similar DC and cytotoxicity compared with EDAB when associated with CQ.
Direct photocuring provided a higher degree of conversion for the self-adhesive resin cement. The delayed light activation did not influence the degree of conversion for the resin cement tested.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.