In recent years, several incidents of cracking and failures have been observed in Stellite (Stellite is a registered trademark of the Deloro-Stellite Corporation) hardfacing used in valves of modern high temperature combined cycle gas fired power plants. These hardfacing layers are applied as an overlay onto a steel substrate, such as CrMo steel (i.e. Grade 22, WC9) or creep strength enhanced ferritic steel (i.e. Grade 91, C12A). Cracking has been observed in valve components at the Stellite/steel interface and in the weld dilution zone formed between the steel and clad. Ultimately, disbonding or delamination of the weld hardfacing from the valve body occurs and has resulted in collateral damage to components in the plant (such as to the turbine) or valve failure. In this study, the microstructure formed near the Stellite/steel interface is investigated. Based on thermodynamic modelling, microstructure formed at these regions is hypothesised and a simple methodology is proposed to predict the occurrence of these failures.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.