We describe four criteria for the selection of alloying elements capable of producing castable, precipitationstrengthened Al alloys with high-temperature stability and strength: these alloying elements must (i) be capable of forming a suitable strengthening phase, (ii) show low solid solubility in Al, (iii) low diffusivity in Al, and (iv) retain the ability for the alloy to be conventionally solidified. With regard to criterion (i), we consider those systems forming Al 3 M trialuminide compounds with a cubic L1 2 crystal structure, which are chemically and structurally analogous to Ni 3 Al in the Ni-based superalloys. Eight elements, clustered in the same region of the periodic table, fulfill criterion (i): the first Group 3 transition metal (Sc), the three Group 4 transition metals (Ti, Zr, Hf) and the four latest lanthanide elements (Er, Tm, Yb, Lu). Based on a review of the existing literature, these elements are assessed in terms of criteria (ii) and (iii), which satisfy the need for a dispersion in Al with slow coarsening kinetics, and criterion (iv), which is discussed based on the binary phase diagrams.

Powder metallurgy was used to fabricate fully dense, unreacted composites consisting of a copper matrix containing 50–60 vol% ZrW2O8 particles with negative thermal expansion. Upon cycling between 25 and 300 °C, the composites showed coefficients of thermal expansion varying rapidly with temperature and significantly larger than predicted from theory. The anomalously large expansion on heating and contraction on cooling are attributed to the volume change associated with the allotropic transformation of ZrW2O8 between its high-pressure γ-phase and its low-pressure α- or β-phases. Based on calorimetry and diffraction experiments and on simple stress estimations, this allotropic transformation is shown to result from the hydrostatic thermal stresses in the particles due to the thermal expansion mismatch between matrix and reinforcement.

No abstract

No abstract