No abstract

Alumina (Al2O3) and zirconia (ZrO2) have good overall properties and thus are widely used oxide technical ceramics. The biggest drawback of Al2O3 is its low fracture toughness. In contrast, ZrO2 is relatively tough, but is also much more expensive. In order to improve the alumina toughness, composite ceramics are being developed. Slip casting technology has economic advantages over the conventional hot isostatic pressure technology, but problems may arise when preparing stable highly-concentrated suspensions (slip) for filling the mold. The purpose of this study is to prepare aqueous suspensions using 70 wt. % α-Al2O3, with 0, 1, 5 and 10 wt. % of added t-ZrO2. Suspensions were electrosterically stabilized using the ammonium salt of polymethylacrylic acid, an alkali-free anionic polyelectrolyte dispersant. Also, magnesium oxide in form of magnesium aluminate spinel (MgAl2O4) was used to inhibit the abnormal alumina grain growth during the sintering process. Minimum viscosities were used as stability estimators, where an increase in ZrO2 content required adding more dispersant. After sintering, the Vickers indentation test was used to determine the hardness and the indentation fracture toughness from the measurement of the crack length. Also, the brittleness index (Bi, μm−1/2) was calculated from values of Vickers hardness and the Vickers indentation fracture toughness. It was found that with increasing ZrO2 content the fracture toughness increased, while the hardness as well as the brittleness index decreased. Zirconia loading reduces the crystallite sizes of alumina, as confirmed by the X-ray diffraction analysis. SEM/EDS analysis showed that ZrO2 grains are distributed in the Al2O3 matrix, forming some agglomerates of ZrO2 and some pores, with ZrO2 having a smaller grain size than Al2O3.

No abstract

The green machining of alumina (Al2O3) green bodies generates a certain amount of waste alumina powder. Waste alumina ceramic powder should be disposed of as non-hazardous waste in a legally compliant manner. The influence of additives on the stability of 70 wt.% (≈40 vol.%) alumina—waste alumina water-based suspension was investigated in the presented research. A Box-Behnken three-factor response surface design was used for the preparation of stable highly-concentrated suspensions with the addition of three additives. The optimal amount of each additive was selected according to the obtained results of minimal apparent viscosity: 0.05 wt.% Tiron as dispersant, 0.1 wt.% poly (vinyl alcohol) as binder and 0.2 wt.% magnesium aluminate spinel as abnormal grain growth inhibitor. The analysis of variance was used to identify the contribution of each additive. The zeta potential and sedimentations tests were performed to confirm the suspension stability measurements at different pH values. Alumina particles were optimally dispersed at pH values between 8 and 11. According to the results, the investigated composition of 20 wt.% waste alumina powder (weight content, dry alumina powder), with the addition of optimal amounts of additives, shows a possible application in the production of ceramics by slip casting.

The plasma-assisted chemical vapor deposition (PACVD) technique has shown many advantages in applications, where thin coatings with superior wear properties are demanded, especially for geometrically complex parts. In this study, multilayered gradient TiBN coatings that were deposited on nanostructured cemented carbides by the PACVD method were investigated. Nanostructured samples of cemented carbides with the addition of 5 and 15 wt.% Co were sintered by the hot isostatic pressing, sinter-HIP technique. Surface preparation was conducted on samples in order to enable maximum coating adhesion. Tests that were conducted on produced samples aimed to investigate the mechanical and physical properties of coated samples. These tests included nanoindentation, surface layer characterization, and coating adhesion evaluation while using the Rockwell and scratch test. The obtained results confirmed that the PACVD process can be utilized for applying thin hard coatings to nanostructured cemented carbides that are produced by the sinter HIP process, resulting in a base material/ coating system that exhibits excellent physical and mechanical properties. The results presented in this paper give a valuable contribution to the research of TiBN coating systems and their potential for application under heavy wear conditions.