Solid-state reaction was used for Li7La3Zr2O12 material synthesis from Li2CO3, La2O3 and ZrO2 powders. Phase investigation of Li7La3Zr2O12 was carried out by x-ray diffraction (XRD), scanning electron microscopy (SEM) and energy-dispersive x-ray spectroscopy (EDS) methods. The thermodynamic characteristics were investigated by calorimetry measurements. The molar heat capacity (Cp,m), the standard enthalpy of formation from binary compounds (ΔoxHLLZO) and from elements (ΔfHLLZO), entropy (S0298), the Gibbs free energy of the Li7La3Zr2O12 formation (∆f G0298) and the Gibbs free energy of the LLZO reaction with metallic Li (∆rGLLZO/Li) were determined. The corresponding values are Cp,m = 518.135 + 0.599 × T − 8.339 × T−2, (temperature range is 298–800 K), ΔoxHLLZO = −186.4 kJ·mol−1, ΔfHLLZO = −9327.65 ± 7.9 kJ·mol−1, S0298 = 362.3 J·mol−1·K−1, ∆f G0298 = −9435.6 kJ·mol−1, and ∆rGLLZO/Li = 8.2 kJ·mol−1, respectively. Thermodynamic performance shows the possibility of Li7La3Zr2O12 usage in lithium-ion batteries.
Александров Даниил Александрович — кандидат биологических наук, профессор, руководитель Лаборатории социологии образования и науки НИУ ВШЭ — СПб. Эл. адрес: d_alexandrov@hse.spb.ru Баранова Влада Вячеславовна — кандидат исторических наук, научный сотрудник Лаборатории социологии образования и науки НИУ ВШЭ — СПб. Эл. адрес: vbaranova@hse.spb.ru Иванюшина Валерия Александровна — кандидат биологических наук, старший научный сотрудник Лаборатории социологии образования и науки НИУ ВШЭ — СПб. Эл. адрес: ivaniushina@hse.spb.ru Представлены результаты первого в России масштабного исследования адаптации детей из семей мигрантов в школах. На основании результатов анализа эмпирического материала обсуждаются вопросы этнической и социальной дифференциации школ, взаимодействия родителей со школой, отношения учителей к иноэтничным ученикам, межэтнического общения школьников.Установлено, что распределение детей по школам в большей степени определяется их социальным положением, чем этническим происхождением. Подтверждены данные американских социологов о том, что существует позитивный отбор мигрантов и что для мигрантов первого поколения характерен так называемый иммигрантский оптимизм. Предполагается, что в России этот эффект обусловлен недавним началом массовой миграции, в связи с чем может быть утрачен в следующем поколении.С использованием метода многоуровневой регрессии продемонстрировано влияние миграционного и этнического статуса на успеваемость. Показано, что дети-мигранты, принадлежащие к этническим меньшинствам, обладают высокой учебной мотивацией и их образовательные результаты не уступают достижениям их местных сверстников в этих же школах, а образовательные планы иноэтничных мигрантов не отличаются от таковых этнического большинства. Результаты анализа сетей общения в классах свидетельствуют об отсутствии в школах дискриминации представителей этнических меньшинств со стороны этнического большинства вопреки существующим в российском обществе националистическим настроениям.Определены перспективы продолжения исследования с точки зрения долгосрочных социальных прогнозов.
Li3FeN2 material was synthesized by the two-step solid-state method from Li3N (adiabatic camera) and FeN2 (tube furnace) powders. Phase investigation of Li3N, FeN2, and Li3FeN2 was carried out. The discharge capacity of Li3FeN2 is 343 mAh g−1, which is about 44.7% of the theoretic capacity. The ternary nitride Li3FeN2 molar heat capacity is calculated using the formula Cp,m = 77.831 + 0.130 × T − 6289 × T−2, (T is absolute temperature, temperature range is 298–900 K, pressure is constant). The thermodynamic characteristics of Li3FeN2 have the following values: entropy S0298 = 116.2 J mol−1 K−1, molar enthalpy of dissolution ΔdHLFN = −206.537 ± 2.8 kJ mol−1, the standard enthalpy of formation ΔfH0 = −291.331 ± 5.7 kJ mol−1, entropy S0298 = 113.2 J mol−1 K−1 (Neumann–Kopp rule) and 116.2 J mol−1 K−1 (W. Herz rule), the standard Gibbs free energy of formation ΔfG0298 = −276.7 kJ mol−1.
Li7La3Zr2O12Solid-state reaction was used for Li7La3Zr2O12 material synthesis from Li2CO3, La2O3 and ZrO2 powders. Phase investigation by XRD, SEM and EDS methods of Li7La3Zr2O12 were carried out. The molar heat capacity of Li7La3Zr2O12 at constant pressure in the temperature range 298-800 K should be calculated as Cp,m = 518.135+0.599 × T - 8.339 × T−2, where T is absolute temperature, . Thermodynamic characteristics of Li7La3Zr2O12 were determined as next: entropy S0298 = 362.3 J mol-1 K-1, molar enthalpy of dissolution ΔdHLlZO = ˗ 1471.73 ± 29.39 kJ mol−1, the standard enthalpy of formation from elements ΔfH0 = ˗ 9327.65 ± 7.9 kJ mol−1, the standard Gibbs free energy of formation ∆f G0298 = ˗9435.6 kJ mol-1.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.