The capability of poly(ethylene-co-methacrylic acid) (E/MAA) to self-heal is well known, however, its mechanical properties are weak. In this study, composites with single and double layers of unidirectional (UD) carbon fibers were prepared by compression molding. Even a low mass fraction of fibers substantially improved the polymer. The flexural and tensile properties were tested at 0°, 45° and 90° fibers direction and compared to those of the matrix. The mechanical properties in the 0° direction proved superior. Flexural properties depended on the reinforcement distance from the stress neutral plane. The tensile modulus in the 0° direction was 13 times greater despite only a 2.5% mass fraction of fibers. However, both tensile modulus and strength were observed to degrade in the 90° direction. Dynamic mechanical analysis showed the dependence of both structure and properties on the thermal history of E/MAA. Tensile tests after ballistic impact showed that the modulus of the self-healed E/MAA was not affected, yet the strength, yield point, and particularly the elongation at break were reduced. A composite with higher fiber content could be prepared by mixing milled E/MAA particles in fibers prior to compression.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.