Wide gap brazing (WGB) is a cost effective and reliable means to repair gas turbine hot section components with defect sizes exceeding 0.3 mm. However, it has been shown that WGB joints of nickel-based superalloys suffer from reduced ductility and thermal fatigue life due to the presence of brittle intermetallics and porosities in the brazed joint. In order to disperse the brittle intermetallic compounds, potentially increase the ductility of the repaired region, and reduce the risk of the thermo-mechanical fatigue failure, elemental tungsten (W) was added to the braze additive filler alloy IN738 by mechanical alloying. The alloyed IN738 was then brazed with the addition of 30, 50 and 80 wt% of braze alloy (BNi-9). After brazing at 1200°C for 20 minutes, microstructural analysis of WGB joints showed a decreasing trend of discrete boride size and the amount of eutectic and script-shaped borides with the increases of W. The increase in the braze alloy to additive filler alloy ratio diminished the effect of W addition due the dissolution of W particulates.
Wide gap brazing (WGB) is a cost effective and reliable means to repair gas turbine hot section components with defect sizes exceeding 0.3 mm. However, it has been shown that WGB joints of nickel-based superalloys suffer from reduced ductility and thermal fatigue life due to the presence of brittle intermetallics and porosities in the brazed joint. In order to disperse the brittle intermetallic compounds, potentially increase the ductility of the repaired region, and reduce the risk of the thermomechanical fatigue failure, elemental tungsten (W) was added to the braze additive filler alloy IN738 by mechanical alloying. The alloyed IN738 was then brazed with the addition of 30 wt %, 50 wt %, and 80 wt % of braze alloy (BNi-9). After brazing at 1200°C for 20 min, microstructural analysis of WGB joints showed a decreasing trend of discrete boride size and the amount of eutectic and script-shaped borides with the increases of W. The increase in the braze alloy to additive filler alloy ratio diminished the effect of W addition due the dissolution of W particulates.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
customersupport@researchsolutions.com
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.