Intensity variation of 1.5 μm light emission at room temperature from Er-doped epitaxial and polycrystal ZnO films depending on annealing temperature (773–1373 K) was studied. As-grown Er-doped epitaxial ZnO film emitted 1.5 μm photoluminescence(PL) higher than as-grown Er-doped polycrystal ZnO. It was found that the annealing in air increases PL intensity and the maximum PL intensity was obtained by annealing at optimal temperature (1073 K). Spectrum shape and intensity of 1.5 μm PL of Er-doped epitaxial ZnO after annealing at 1073 K resembled those of Er-doped polycrystal ZnO after annealing at 1073 K. X-ray diffraction measurement demonstrated that annealing improves crystal quality of Er-doped ZnO film. We assumed that the process of 1.5 μm light emission is dependent on local area placement of Zn and O atoms around Er as well as crystal quality of ZnO.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.