The cast Al-Mg2Si metal matrix composite was prepared by metal model casting process with rare earth element Nd as the modificator. The effects of modification duration and remelting times on microstructure and mechanical properties of the composite were investicated by optical microscope (OM) and electronic universal testing machine. The results show that, after introducing a proper amount of Nd, both primary and eutectic Mg2Si in the Al-18 wt.%Mg2Si composite were well modified. The morphology of primary Mg2Si is changed from irregular or dendritic to polyhedral shape and the morphology of the eutectic Mg2Si phase is altered from flake-like to very short fibrous or dot-like. Moreover, the effect is of long-lasting and remelting properties. After the composite is modified for 300 min and remelted by 6 times, its primary and eutectic Mg2Si structures are still in modification state of small block and slices, and the tensile properties of the composite are not significantly affected.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.