In the present study our interest is focused on finding the efficiency of 60SiO2·(32 - x)CaO·8P2O5·xCuO (mol%) glass-ceramics, with 0 ≤ x ≤ 4 mol%, in terms of bioactivity, biocompatibility, antibacterial properties and cell viability in order to determine the most appropriate composition for their further use in in vivo trials. The sol-gel synthesized samples show a preponderantly amorphous structure with a few crystallization centers associated with the formation of an apatite and calcium carbonate crystalline phases. The Fourier Transform Infrared (FT-IR) spectra revealed slightly modified absorption bands due to the addition of copper oxide, while the information derived from the measurements performed by transmission electron microscopy, UV-vis and electron paramagnetic resonance spectroscopy showed the presence of ions and metallic copper species. X-Ray photoelectron spectroscopic analysis indicated the presence of copper metallic species, in a reduced amount, only on the sample surface with the highest Cu content. Regarding in vitro assessment of bioactivity, the results obtained by X-ray diffraction, FT-IR spectroscopy and scanning electron microscopy, demonstrated the formation of a calcium phosphate layer on all investigated sample surfaces. The inhibitory effect of the investigated samples was more significant on the Pseudomonas aeruginosa than the Staphylococcus aureus strain, the sample with the lowest concentration of copper oxide (0.5 mol%) being also the most efficient in both bacterial cultures. This sample also exhibits a very good bactericidal activity, for the other samples it was necessary to use a higher quantity to inhibit and kill the bacterial species. The secondary structure of adsorbed albumin presents few minor changes, indicating the biocompatibility of the glass-ceramics. The cell viability assay shows a good proliferation rate on samples with 0.5 and 1.5 mol% CuO, although all glass-ceramic samples exhibited a good in vivo tolerance.
This study is focused on structural changes induced by increasing treatment temperature of sol-gel-derived 4 , and AlO 6 , and starting with 800°C treatment also of BO 4 and AlO 5 structural units, but more detailed information related to boron, aluminum, and gallium environments is obtained from the analysis of MAS-NMR data. These data evidenced in both amorphous xerogels and in crystallized samples a high fraction of penta-coordinated aluminum and gallium.
Abstract:The effects of gamma radiation on the local structure of PVA membranes containing TiO 2 were investigated by ESR and XRD methods. An intense ESR signal is observed after irradiation at 16 KGy dose. This signal appears only for irradiated samples and it is associated with the breaking of the polymeric chain, followed by local reorganization of the polymeric segments and the apparition of the unpaired electrons and free radicals. The intensity of the signal decreases with the concentration of TiO 2 , indicating a shielding effect of the dopand. That the modification of local order of the polymeric chains has been modified after irradiation is confirmed by XRD method.
PACS
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.