Critical-sized defects (CSDs) were introduced into rat calvaria to test the hypothesis that absorption of surrounding blood, marrow, and fluid from the osseous wound into a bioabsorbable polymer matrix with unique microarchitecture can induce bone formation via hematoma stabilization. Scaffolds with 90% porosity, specific surface areas of approximately 10 m2/g, and median pore sizes of 16 and 32 microm, respectively, were fabricated using an emulsion freeze-drying process. Contact radiography and radiomorphometry revealed the size of the initial defects (50 mm2) were reduced to 27 +/- 11 mm2 and 34 +/- 17 mm2 for CSDs treated with poly(D,L-lactide-co-glycolide). Histology and histomorphometry revealed scaffolds filled with significantly more de novo bone than negative controls (p < 0. 007), more osteoid than both the negative and autograft controls (p < 0.002), and small masses of mineralized tissue (< 15 mm in diameter) observed within the scaffolds. Based on these findings, we propose a change in the current paradigm regarding the microarchitecture of scaffolds for in vivo bone regeneration to include mechanisms based on hematoma stabilization.
Drug delivery devices have received considerable interest in the field of tissue engineering due to the advent of proteins that can induce proliferation and differentiation of various cells to form specific tissues and organs, for example, bone morphogenetic protein (BMP-2) for osteogenesis. In this work the delivery of a clinically relevant bioactive factor, recombinant human rhBMP-2, was tested in vivo in a rat ectopic bone induction assay. Contact radiography and radiomorphometry showed significantly more radiopacity (1798+/-183 mm2 versus. 784+/-570 mm2 radiopaque area/g scaffold) in the BMP scaffolds than controls (p < 0.002). De novo woven bone and abundant osteoid formation were confirmed from histological sections while controls contained minimal amounts of tissue. Histomorphometry revealed significantly more bone (124+/-93 mm2 versus 7+/-12 mm2) and osteoid (72+/-43 mm2 versus 20+/-21 mm2) in the BMP implants (p < 0.001). These scaffolds demonstrated the ability to deliver viable rhBMP-2 and to induce bone formation in an ectopic site.
An emulsion method was developed for the incorporation of water-soluble mitomycin C into polylactic acid biodegradable microcapsules. With an average particle size of about 95 microns, microcapsules with a desired loading of from 3.65 to 13.80 per cent were prepared. These microcapsules, which contained both crystalline and finely dispersed drug particles, showed a dose-dependent drug release pattern with microcapsules of higher drug loading having a faster release rate than those of lower drug loading. Effective sterilization of the microcapsules for parenteral use was achieved by 60Co gamma-ray irradiation, which did not affect the microcapsule structure, release rate or drug stability. Mitomycin C showed dose-dependent antiproliferative activity against the growth of the K562 human erythroleukaemia cells. The microencapsulated dosage form of mitomycin C was found to enhance the drug's activity through sustained drug release. In experiments where drug concentrations in the cell medium were reduced according to the drug's biological half-life, the microcapsule systems showed a distinct advantage over the non-capsulated dose for the kinetic inhibition of K562 cell growth.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.