The early failure and revision of bimodular primary total hip arthroplasty prostheses requires the identification of the risk factors for material loss and wear at the taper junctions through taper wear analysis. Deviations in taper geometries between revised and pristine modular neck tapers were determined using high resolution tactile measurements. A new algorithm was developed and validated to allow the quantitative analysis of material loss, complementing the standard visual inspection currently used. The algorithm was applied to a sample of 27 retrievals (in situ from 2.9 to 38.1 months) of the withdrawn Rejuvenate modular prosthesis. The mean wear volumes on the flat distal neck piece taper was 3.35 mm3 (0.55 to 7.57), mainly occurring in a characteristic pattern in areas with high mechanical loading. Wear volume tended to increase with time to revision (r² = 0.423, p = 0.001). Implant and patient specific data (offset, stem size, patient’s mass, age and body mass index) did not correlate with the amount of material loss observed (p >  0.078). Bilaterally revised implants showed higher amounts of combined total material loss and similar wear patterns on both sides. The consistent wear pattern found in this study has not been reported previously, suggesting that the device design and materials are associated with the failure of this prosthesis. Cite this article: Bone Joint J 2015;97-B:1350–7.

No abstract

Bi-modular primary hip stems exhibit high revision rates owing to corrosion at the stem-neck taper, and are associated with local adverse tissue reactions. The aim of this study was to relate the wear patterns observed for one bi-modular design to its design-specific stem-neck taper geometry. Wear patterns and initial geometry of the taper junctions were determined for 27 retrieved bi-modular primary hip arthroplasty stems (Rejuvenate, Stryker Orthopaedics) using a tactile coordinate-measuring device. Regions of high-gradient wear patterns were additionally analyzed via optical and electron microscopy. The determined geometry of the taper junction revealed design-related engagement at its opening (angle mismatch), concentrated at the medial and lateral apexes (axes mismatch). A patch of retained topography on the proximal medial neck-piece taper apex was observed, surrounded by regions of high wear. On the patch, a deposit from the opposing female stem taper-containing Ti, Mo, Zr, and O-was observed. High stress concentrations were focused at the taper apexes owing to the specific geometry. A medial canting of the components may have augmented the inhomogeneous stress distributions in vivo. In the regions with high normal loads interfacial slip and consequently fretting was inhibited, which explains the observed pattern of wear.

No abstract