A simple and straightforward method using microwave-assisted reactions is presented for the functionalization of graphene oxide with aromatic and non-aromatic amines.
Binary, ternary and quaternary electrocatalysts of type C/Pt-based were prepared by the Pechini method. The physical-chemical characterization and electrochemical investigation of the electrocatalysts were performed by different techniques: X-ray diffraction, cyclic voltammetry and chronoamperometry. The XRD results show that the electrocatalysts are mainly formed by Pt metal structure with face-centered cubic crystalline. The electrocatalysts were evaluated in the absence and presence of glycerol in sulfuric acid medium. The ternary electrocatalyst composition in which platinum is greater than 70 mol% showed the highest values of current density during the chronoamperometry studies. The catalyst C/Pt70Ru20Ni10 showed the most significant peaks of oxidation of glycerol and its intermediates products in VC: in the positive-going scan and in the negative-going scan.
Electrocatalysts of type PtSnNiTi/C were prepared by thermal decomposition of polymeric precursors. The physico-chemical and electrochemical characterization of the electrocatalysts was performed by different techniques: X-ray diffraction, transmission electron microscopy, cyclic voltammetry and chronoamperometry. The XRD results showed that the electrocatalysts comprise mainly Pt metal with face-centered cubic crystal structure. The electrocatalysts were evaluated in the absence and presence of ethanol and glycerol in sulfuric acid medium. All showed activity toward alcohols oxidation. Furthermore, the Pt50Sn20Ni25Ti5/C electrocatalyst showed the best results of cyclic voltammetry and chronoamperometry in presence of glycerol and ethanol, respectively. Cyclic voltammetry data obtained in this study indicate that the addition of Ni and Ti in PtSn electrocatalysts increases its electrocatalytic activity toward alcohols oxidation. For alcohol (ethanol and glycerol) electrooxidation, high performance liquid chromatography (HPLC) was carried out after electrolysis, for determination of the products generated from alcohol consumption. The main product found after electrolysis was acetaldehyde.
Porous carbon materials were prepared at low temperatures via thermal decomposition of iron, nickel and cobalt N,N-diethyldithiocarbamates (DDT). X-ray diffraction data showed two peaks at 2θ (25.5° and 43.5°) that indicate the presence of graphite-like structures. Raman spectra displayed D and G bands in the range from 1312 to 1321 cm -1 and 1587 to 1593 cm -1 , respectively, which were fitted with 4 components. All spectra showed two low intensity D* (1190 cm ) bands, assigned to sp 2 -sp 3 bonds in disordered carbonaceous materials and amorphous carbon, respectively. Transmission electron microscopy images showed agglomerates of spherical particles formed by graphitic segments. The results showed that the carbon material obtained from iron N, N-diethyldithiocarbamate, Fe(DDT) 3 , is structurally better organized than the others and the pore size distribution curves confirmed that this material presents high degree of mesoporosity. Voltammetric curves obtained using KOH and H 2 SO 4 electrolytes showed hysteresis behavior typical of capacitors charge/discharge process. The carbon material prepared from Fe(DDT) 3 displayed the highest specific capacitance in acidic media, 59 F g -1 , which was associated to its high degree of mesoporosity. Keywords: carbon materials, diethyldithiocarbamate complexes, electrochemical application IntroductionDifferent physical methods have been used to prepare carbon nanomaterials such as laser ablation, 1,2 arch discharge 3,4 and combustion. 5,6 Thermal decomposition of organic and organometallic precursors [7][8][9] has been presented as a viable alternative to physical methods which use harsh synthesis conditions and yield small amount of products. Different carbon-rich precursors are used to obtain these carbon nanostructures, which can be transformed into graphitic carbon materials of different sizes and shapes. Among these organic precursors, alkynes olygoine derivatives are good candidates due to their high chemical instability, which allows them to undergo different chemical reactions. 10 Various carbon precursors such as benzene, 11 sucrose 12 and phenol resin, 13 are also suitable for the synthesis of carbon materials. Similarly, the pyrolysis of organometallic precursors, such as cobalt acetylacetonate, 14 also yields carbon nanostructures presenting good electrochemical performance which depends on surface area as well as the porosity of these structures. The major problem associated with the method described above is the presence of encapsulated metals.Porous carbon materials are excellent candidates for electrodes in supercapacitors. 15,16 For these materials pore accessibility plays a significant role in the charge storage and the specific capacitance reaches a maximum value when the pore size matches the maximum electrolyte ion dimension. 17 For carbon nanomaterials the surface areas range from 300 to 600 m 2 g -1 and are responsible for electrolyte wetting and rapid ionic motions necessary for da Silva et al. 1905 Vol. 29, No. 9, 2018 a satisfactory electroc...
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.