No abstract

No abstract

The influence of 1,2 vinyl content on hydrogenation of SBR and BR rubbers with high molecular weight by a noncatalytic method using p-toluenesulfonylhydrazide (TSH) as reagent was investigated. Results show an increase of hydrogenation percentage with molar ratio of the reagents, temperature, and reaction time. The degree of hydrogenation depends strongly on the microstructure of the rubber mainly on the amount of 1,2 content. Infrared spectroscopy (FTIR) was used to confirm the microstructural characteristics of the hydrogenated rubbers. The degree of hydrogenation was determined by iodometry method and 1 H-NMR analysis. The change in the thermal behavior of hydrogenated rubbers was followed by differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA), which showed a difference in flexibility chain and thermal stability. The kinetic studies demonstrate that the diimide reduction follows a firstorder reaction with respect to olefin substrate.

ResumoO acúmulo de poliestireno expandido (EPS) em sua forma pós-consumo é atualmente um motivo de preocupação em termos de impacto ambiental. Desenvolve-se, portanto, diferentes formulações de uma resina veículo para tinta que aproveitam este material como matéria-prima, através da dissolução do mesmo em solventes de origem natural extraídos da casca de laranja, quais sejam o próprio óleo essencial e seu componente majoritário D-limoneno, e em C9 aromático, junto aos copolímeros termoplásticos ESBR, SIS, SBS e SEBS e óleo de soja epoxidado (ESBO) como plastificantes. Obtém-se, em diferentes formulações, um desempenho favorável à futura adição de pigmento e demais aditivos, em termos de compatibilidade, elasticidade e aderência avaliados conforme normatização nacional e internacional. Observa-se especial sucesso com o uso do copolímero SEBS e do ESBO como plastificantes, concomitantemente à eficiência semelhante dos três solventes utilizados, o que permite a substituição do C9 aromático por componentes de origem natural e residual. Palavras-chave: Poliestireno expandido; D-limoneno; Polímeros; Tinta. DEVELOPMENT OF RESIN BASED ON RESIDUAL EXPANDED POLYSTYRENE (EPS) AbstractThe accumulation of expanded polystyrene (EPS) postconsumer is currently a reason for preoccupation in terms of environmental impact. Thereby, varied formulations of a vehicle resin for paint are developed and utilize this as a raw material, through its dissolution in natural solvents extracted of orange peels, namely the very essential oil and its main component D-limonene, and in C9 aromatic, along with thermoplastic copolymers ESBR, SIS, SBS and SEBS and epoxidized soybean oil (ESBO) as plasticizer. In different formulations, it is obtained a favorable performance for future addition of pigments and other additives, in terms of compatibility, elasticity and adhesion evaluated according national and international standardization. Special success was observed with the use of copolymer SEBS and ESBO as plasticizers, simultaneously to the similar efficiency of the three solvents that were used, which allows the substitution of C9 aromatic with components with natural and residual origins.

Neste trabalho, desenvolveu-se uma espuma de poliuretano com poliol que foi obtida a partir do óleo de linhaça. Para a síntese do poliol, o método de epoxidação e hidroxilação do óleo de linhaça foi utilizado em uma única etapa, a partir do ácido perfórmico, gerado in situ, na relação molar de HCOOOH/H2O2/C=C igual a 3/1,5/1. A caracterização do poliol de óleo de linhaça deu-se através do índice de hidroxila, funcionalidade e espectro infravermelho, mostrando ser adequado para síntese de PU. A espuma PU desenvolvida foi sintetizada na proporção molar [NCO/OH] de 1,5 e caracterizada quanto à densidade, à morfologia, à reatividade e às propriedades mecânicas, apresentando propriedades similares às espumas comerciais semirrígidas. Palavras-chave: síntese polimérica; poliuretano, óleo de linhaça.