Phase behavior of aqueous systems containing block copolymers of poly(ethylene oxide (PEO) and poly(propylene oxide) (PPO) was evaluated by building up temperature-concentration phase diagrams. We have studied bifunctional triblock copolymers (HO-PEO-PPO-PEO-OH) and monofunctional diblock copolymers (R-PEO-PPO-OH and R-PPO-PEO-OH, where R length is linear C 4 and C 12-14 ). The cloud points of the polymer solutions depended on EO/PO ratio, polarity, R length and position of the hydrophilic and hydrophobic segments along the molecule. Such factors influence on the solutions behavior was also analyzed in terms of critical micelle concentration (CMC), which was obtained from surface tension vs. concentration plots. Salts (NaCl and KCl) added into the polymer solutions change the solvent polarity decreasing the cloud points. On the other hand, the cloud points of the polymer solutions increased as a hydrotrope (sodium p-toluenesulfonate) was added.
ABSTRACT:The effect of the hydrotropic agent, sodium p-toluenesulfonate (NaPTS), was evaluated on the micelle formation process and on phase behavior of aqueous solutions containing poly(ethylene oxide-b-propylene oxide) (PEO-PPO) copolymers. We have studied monofunctional diblock copolymers coupled with hydrocarbons groups (R{PEO{PPO{OH and R{PPO{PEO{OH, where R length is linear C 4 and C 12-14 ). The critical micelle concentration (CMC) and critical micelle temperature (CMT) values of the aqueous copolymers solutions were obtained from both surface tension versus concentration plots and the dye solubilization method. The influence of the hydrocarbons groups length and PPO segment position in the structure of the copolymers were also analyzed. The same measures were obtained for the aqueous solutions of hydrotropic agent which, in turn, also presented molecular aggregation. The presence of the hydrotropic agent in the aqueous copolymers solutions altered the surface tension of these solutions and the occupied molecular area per copolymer molecule at air-water interface and CMC and CMT values of the copolymers. On the other hand, the aggregation points and the surface tension of the NaPTS solutions were dependent on the copolymer structure and composition.
The thermal degradation of some blends of polyamide 6/polycarbonate (PA6/PC) and polyamide 6/polycarbonate/poly(propylene oxide) (PA6/PC/PPO) were investigated. The copolymer formed during the mixing of polyamide 6 and polycarbonate, at 240°C, for 30 min, increases the thermal stability of PA6/PC and of PA6/PC/PPO blends. This increase in the thermal stability occurs due to the plasticizing effect of PPO, which increases the mobility of the molecules of PA6 and PC, and consequently increases the probability of the reaction between the -NH 2 and -O-CO-O groups of polyamide 6 and polycarbonate, respectively. The ternary blends with PPO (5-10% w/w) have lower thermal stability than PA6/PC blends. This is due to the decrease of miscibility between these polymers and the rise of the diluting effect.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.