A systematic approach has been followed in the development of a high-efficiency hybrid photovoltaic device that has a combination of poly(3-hexylthiophene) (P3HT), [6,6]-phenyl C61-butyric acid methyl ester (PCBM), and silver nanowires (Ag NWs) in the active layer using the bulk heterojunction concept. The active layer is modified by utilizing a binary solvent system for blending. In addition, the solvent evaporation process after spin-coating is changed and an Ag NWs is incorporated to improve the performance of the hybrid photovoltaic device. Hybrid photovoltaic devices were fabricated by using a 1:0.7 weight ratio of P3HT to PCBM in a 1:1 weight ratio of o-dichlorobenzene and chloroform solvent mixture, in the presence and absence of 20 wt % of Ag NWs. We also compared the photovoltaic performance of Ag NWs embedded in P3HT:PCBM to that of silver nanoparticles (Ag NPs). Atomic force microscopy, scanning electron microscopy, transmittance electron microscopy, UV-visible absorption, incident photon-to-current conversion efficiency, and time-of-flight measurements are performed in order to characterize the hybrid photovoltaic devices. The optimal hybrid photovoltaic device composed of Ag NWs generated in this effort exhibits a power conversion efficiency of 3.91%, measured by using an AM 1.5G solar simulator at 100 mW/cm(2) light illumination intensity.
요약. 형광체나 반도체의 소자로 사용되는 전이금속화합물 중에서 나노(nano)크기를ABSTRACT. The spinel compound was obtained by the thermal decomposition of Zn-Co and Zn-Ni gel prepared by sol-gel method using oxalic acid as a chelating agent. The formation of spinel compound has been comfirmed by thermogravimetric analysis (TGA), x-ray powder diffraction (XRD) and infrared spectroscopy (IR). The particle size of 13 nm∼16 nm was calculated by Scherrer`s equation. The sol-gel method provides a practicable and effective route for the synthesis of the spinel compound at low temperature (350 o C). The kinetic parameters such as activation energy (Ea) and pre-exponential factor (A) for each compound were found by means of the Kissinger method and Arrhenius equation.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.