Metal additive manufacturing techniques are frequently applied to the manufacturing of injection molds with a conformal cooling channel (CCC) in order to shorten the cooling time in the injection molding process. Reducing the cooling time in the cooling stage is essential to reducing the energy consumption in mass production. However, the distinct disadvantages include higher manufacturing costs and longer processing time in the fabrication of injection mold with CCC. Rapid tooling technology (RTT) is a widely utilized technology to shorten mold development time in the mold industry. In principle, the cooling time of injection molded products is affected by both injection mold material and coolant medium. However, little work has been carried out to investigate the effects of different mold materials and coolant media on the cooling performance of epoxy-based injection molds quantitatively. In this study, the effects of four different coolant media on the cooling performance of ten sets of injection molds fabricated with different mixtures were investigated experimentally. It was found that cooling water with ultrafine bubble is the best cooling medium based on the cooling efficiency of the injection molded parts (since the cooling efficiency is increased further by about 12.4% compared to the conventional cooling water). Mold material has a greater influence on the cooling efficiency than the cooling medium, since cooling time range of different mold materials is 99 s while the cooling time range for different cooling media is 92 s. Based on the total production cost of injection mold and cooling efficiency, the epoxy resin filled with 41 vol.% aluminum powder is the optimal formula for making an injection mold since saving in the total production cost about 24% is obtained compared to injection mold made with commercially available materials.

Friction welding (FRW) is a promising method for joining cylindrical components of dissimilar and similar polymers or metals. In particular, FRW is capable of generating defect-free welds. Fused deposition modeling (FDM) has been widely employed in the automotive industry, ranging from lightweight tools, testing models, and functional parts. Conventionally, dissimilar parts fabricated by FDM are joined by glue. However, distinct disadvantages of this approach include both low joining strength and low joining efficiency. Hitherto, little has been reported on the characterizations of weld strength of FRW of dissimilar parts fabricated by FDM. In addition, FRW of dissimilar polymeric materials is a difficult task because different polymers have different physical, rheological, and mechanical properties. In this study, the effects of welding revolution on the weld strength of friction welding dissimilar parts fabricated by FDM are investigated experimentally. It was found that the average flexural strength of dissimilar polymer rods fabricated by FRW is about 1.52 times that of dissimilar polymer rods fabricated by gluing. The highest flexure strength can be obtained by FRW using polylactic acid (PLA) and PC (polycarbonate) rods. The average impact strength of dissimilar polymer rods fabricated by FRW is about 1.04 times that of dissimilar polymer rods joined by gluing. The highest impact strength can be obtained by FRW using PLA to PLA rods.

Friction welding (FW) FW of dissimilar polymer rods is capable of manufacturing green products swiftly and economically. In this study, a green manufacturing technique of joining dissimilar polymer rods was proposed, and the effects of rotational speed on the joint characteristics of friction-welded dissimilar polymer rods fabricated by the fused deposition modeling process were investigated experimentally. The shore surface hardness test, impact test, three-point bending test, and differential scanning calorimetry analysis were carried out on the weld joints. The impact energy for FW of polylactic acid (PLA) and PLA, PLA and acrylonitrile butadiene styrene (ABS), PLA and PLA filled with glass fiber (GF), PLA and PLA filled with carbon fiber (CF), PLA and polycarbonate (PC), and PLA and polyamide (PA) rods can be increased by approximately 1.5, 1.5, 1.3, 1.3, 2.1, and 1.5 times by increasing the rotational speed from 330 rpm to 1350 rpm. The bending strength for FW of PLA and PLA, PLA and ABS, PLA and PLA filled with GF, PLA and PLA filled with CF, PLA and PC, and PLA and PA rods can be increased by approximately 1.3, 1.7, 1.3, 1.2, 1.2, and 1.2 times by increasing the rotational speed from 330 rpm to 1350 rpm. However, the surface hardness of the weld bead is not proportional to the rotational speed. The average surface hardness of the weld bead was increased by approximately 5% compared to the surface hardness of the welding base materials.