Catalytic water splitting to hydrogen and oxygen is considered as one of the convenient routes for the sustainable energy conversion. Bifunctional catalysts for the electrocatalytic oxygen reduction reaction (ORR) and the oxygen evolution reaction (OER) are pivotal for the energy conversion and storage, and alternatively, the photochemical water oxidation in biomimetic fashion is also considered as the most useful way to convert solar energy into chemical energy. Here we present a facile solvothermal route to control the synthesis of amorphous and crystalline cobalt iron oxides by controlling the crystallinity of the materials with changing solvent and reaction time and further utilize these materials as multifunctional catalysts for the unification of photochemical and electrochemical water oxidation as well as for the oxygen reduction reaction. Notably, the amorphous cobalt iron oxide produces superior catalytic activity over the crystalline one under photochemical and electrochemical water oxidation and oxygen reduction conditions.

A systematic structural elucidation of the near-surface active species of the two remarkably active nickel phosphides Ni12P5 and Ni2P on the basis of extensive analytical, microscopic, and spectroscopic investigations is reported. The latter can serve as complementary efficient electrocatalysts in the hydrogen (HER) versus oxygen evolution reaction (OER) in alkaline media. In the OER Ni12P5 shows enhanced performance over Ni2P due to the higher concentration of nickel in this phase, which enables the formation of an amorphous NiOOH/Ni­(OH)2 shell on a modified multiphase with a disordered phosphide/phosphite core. The situation is completely reversed in the HER, where Ni2P displayed a significant improvement in electrocatalytic activity over Ni12P5 owing to a larger concentration of phosphide/phosphate species in the shell. Moreover, the efficiently combined use of the two nickel phosphide phases deposited on nickel foam in overall electrocatalytic water splitting is demonstrated by a strikingly low cell voltage and high stability with pronounced current density, and these catalysts could be an apt choice for applications in commercial alkaline water electrolysis.

Nanostructured titanium dioxide is one of the classic materials for photoelectrochemical water splitting. In the present work we dope TiO(2) nanotube anodes. For this, various low concentration bulk-Nb-doped TiO(2) nanotube layers were grown by self-organizing anodization of Ti-Nb alloys. At Nb-contents around 0.1 at%, and after an adequate heat-treatment, a strongly increased and stable photoelectrochemical water-splitting rate is obtained.

No abstract

In this work, solar cells with a freshly made CH NH PbI perovskite film showed a power conversion efficiency (PCE) of 15.4 % whereas the one with 50 days aged perovskite film only 6.1 %. However, when the aged perovskite was covered with a layer of Al O deposited by atomic layer deposition (ALD) at room temperature (RT), the PCE value was clearly enhanced. X-ray photoelectron spectroscopy study showed that the ALD precursors are chemically active only at the perovskite surface and passivate it. Moreover, the RT-ALD-Al O -covered perovskite films showed enhanced ambient air stability.

The present work shows a significant enhancement of the photoelectrochemical water-splitting performance of anodic TiO(2) nanotube layers grown on low concentration (0.01-0.2 at% Ru) Ti-Ru alloys. Under optimized preparation conditions (0.05 at% Ru, 450 °C annealing) the water splitting rate of the oxide tubes could be 6-fold increased. Moreover, the beneficial effect is very stable with illumination time; this is in contrast to other typical doping approaches of TiO(2).

Sodium‐ion batteries (NIBs) are promising energy‐storage devices with advantages such as low cost and highly abundant raw materials. To probe the electrochemical properties of NIBs, sodium metal is most frequently applied as the reference and/or counter electrode in state‐of‐the‐art literature. However, the high reactivity of the sodium metal and its impact on the electrochemical performance is usually neglected. In this study, it is shown that spontaneous reactions of sodium metal with organic electrolytes and the importance of critical interpretation of electrochemical experiments is emphasized. When using sodium‐metal half‐cells, decomposition products contaminate the electrolyte during the electrochemical measurement and can easily lead to wrong conclusions about the stability of the active materials. The cycling stability is highly affected by these electrolyte contaminations, which is proven by comparing sodium‐metal‐free cell with sodium‐metal‐containing cells. Interestingly, a more stable cycling performance of the Li4Ti5O12 half‐cells can be observed when replacing the Na metal counter and reference electrodes with activated carbon electrodes. This difference is attributed to the altered properties of the electrolyte as a result of contamination and to different surface chemistries.

Room temperature partial oxidation (corrosion) of cubic CoO led to the formation of mixed valence CoOx with better electrochemical water oxidation activities in alkaline pH. Activation of both octahedral Co3+ and Co2+ to layered oxohydroxide–hydroxide during alkaline electrochemical water oxidation has been demonstrated.