The physical and dielectric properties of composites of known microwave materials, Zn 2 SiO 4 and Zn 3 B 2 O 6 , prepared by solid-state reaction, were investigated with the purpose of developing a low-loss dielectric material for low-temperature co-fired ceramic applications. An off-stoichiometric phase of Zn 2 SiO 4 with extra SiO 2 was used to avoid the occurrence of unreacted ZnO. During sintering, zinc borate was found to partially react with residual SiO 2 to form Zn 2 SiO 4 . The residual zinc borate was converted to a boron-rich glassy phase which helped to reduce the sintering temperature of the composite. Good relative sintering density (>90%) at temperatures below the melting temperature of zinc borate is indicative of a sintering mechanism of diffusion-based mass transfer. Composites containing 15 wt.% zinc borate, 2.5 wt.% lithium carbonate and 20 wt.% zinc borate in zinc silicate had dielectric constants of 6.8 and 6.1, quality factors (Q9f) of 48,800 and 94,300 GHz when sintered at 900°C and 950°C, respectively. These quality factor results are close to the best values reported for zinc silicate at these sintering temperatures.
Single-walled carbon nanotubes (SWNTs) with highly graphitized structure were synthesized by thermal chemical vapor deposition using an improved nitrogen-pretreated FeMo/ MgO catalyst. The effects of nitrogen pretreatment of FeMo/ MgO on the structure and properties of SWNTs were studied by TEM, Raman spectroscopy, and TGA. The investigations revealed that the nitrogen pretreatment of the catalyst promoted the growth of SWNTs. It also enhanced the structural features and thermal properties of SWNTs.Since their discovery in 1991, 1 carbon nanotubes (CNTs) have been ruling the regime of nanoresearch for their remarkable structural, mechanical, thermal, electronic, and phonon properties.2 It is because of these excellent properties, CNTs find their use in several applications such as high strength composites, catalytic reactions, hydrogen storage, field-emission displays, sensors, and so on.3 Depending on the requirement of a particular application, CNTs are modified suitably by a postsynthesis functionalization or during the synthesis itself by controlling the process conditions. In the later case, CNTs are preferably synthesized by chemical vapor deposition (CVD). Among all methods of CNT synthesis, CVD is very amenable due to its flexibility in manipulating reaction parameters. 4 In a conventional CVD process, a transition-metal-based catalyst is activated in inert atmosphere to synthesize CNTs from a gaseous hydrocarbon. Several CVD methods have been reported for the synthesis of CNTs, including those at varying catalyst formulation and reaction parameters.5 Chiral selective growth of single-walled CNTs (SWNTs) can be achieved during nucleation by changing the catalyst composition or structure and controlling the kinetic parameters.6 CNTs doped with N 2 by introducing N 2 gas flow in the flow of reactant gases have also been studied for structural changes, mechanical applications, and catalytic reactions.7 In this letter, we report the synthesis of highly graphitized SWNTs by employing improved nitrogen-pretreated FeMo/MgO catalyst nanoparticles in a thermal CVD and study the effects of nitrogen pretreatment of the catalyst on the structure and properties of SWNTs. We demonstrate herein that simple nitrogen pretreatment can enhance the catalytic activity, which in turn can promote the CNT growth mechanism to form long length, highly graphitized CNTs.The FeMo/MgO catalyst containing 5 wt % of FeMo in 9:1 ratio was prepared from Fe(NO 3 ) 3 ¢9H 2 O (98+%, SigmaAldrich), (NH 4 ) 6 Mo 7 O 24 ¢4H 2 O (99.98%, Sigma-Aldrich), and MgO nanopowder (Strem Chemicals). In a typical procedure, 0.5 g of MgO was taken in 10 mL of methanol and ultrasonicated for 20 min to obtain a suspension. In another beaker, 0.1628 g of Fe(NO 3 ) 3 ¢9H 2 O and 0.0046 g of (NH 4 ) 6 Mo 7 O 24 ¢4H 2 O were mixed in 10 mL of methanol and ultrasonicated for 20 min to obtain a solution. This freshly prepared solution was added dropwise to the suspension of MgO under magnetic stirring at room temperature. The stirring was continued until methanol...
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.
hi@scite.ai
10624 S. Eastern Ave., Ste. A-614
Henderson, NV 89052, USA
Copyright © 2024 scite LLC. All rights reserved.
Made with 💙 for researchers
Part of the Research Solutions Family.