The solubility of single-walled carbon nanotube (SWCNT) polyelectrolytes [K(THF)]nSWCNT in dimethyl sulfoxide (DMSO) was determined by a combination of centrifugation, UV-vis spectral properties, and solution extraction. The SWCNT formed a liquid crystal at a concentration above 3.8 mg/mL. Also, crown ether 18-crown-6 was found to increase the solubility of the SWCNT polyelectrolytes in DMSO. Raman spectroscopy and near-infrared (NIR) fluorescence analyses were applied to study the functionalization of SWCNTs. Small-diameter SWCNTs were found to be preferentially functionalized when the SWCNT polyelectrolytes were dispersed in DMSO.

In this work, single-walled carbon nanotube (SWCNT) fibers were produced from SWCNT polyelectrolyte dispersions stabilized by crown ether in dimethyl sulfoxide and coagulated into aqueous solutions. The SWCNT polyelectrolyte dispersions had concentrations up to 52 mg/mL and showed liquid crystalline behavior under polarized optical microscopy. The produced SWCNT fibers are neat (i.e., not forming composites with polymers) and showed a tensile strength up to 124 MPa and a Young's modulus of 14 GPa. This tensile strength is comparable to those of SWCNT fibers spun from strong acids. Conductivities on the order of 10(4) S/m were obtained by doping the fibers with iodine.

No abstract