Ti-Al-Si-Cu-N nanocomposite films with different Cu contents were deposited on AISI-304 stainless steel by DC reactive magnetron sputtering. Both Ti-Al-SiN and Ti-Al-Si-Cu-N nanocomposite films were oxidized at 800 °C to investigate the influence of Cu content on the microstructure and high temperature oxidation resistance by scanning electron microscope (SEM), energy disperse spectroscopy (EDS), X-ray diffraction (XRD), nanoindentation tester and a home-made indentation system. The results indicate that with the increasing copper content in the films, the micropores disappear on the surface of Ti-Al-SiN nanocomposite film and compact films are obtained. A reduction of the grain size and a change of the (111) preferred orientation to (110) are observed. The microhardness of films increases from 14.76 GPa to 19.42 GPa. The elasticity modulus of Ti-Al-Si-Cu-N films with 1.72 at% Cu content is the minimum of 104.5 GPa. The incorporation of copper at high temperature influences the oxidation resistance of the Ti-Al-SiN films in the two aspects, one is advancing the diffusion rate of Al element, and the other is inducing cracks of oxide layer and micropores. Ti-Al-SiN films have a better oxidation resistance than that of the films added Cu element.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.