fabrication of uniform vertically-aligned titanium dioxide nanorods (tio 2 nRs) was achieved by hydrothermal growth on a fluorine-doped tin oxide (FTO) glass substrate. The substrate was coated by a tio 2 seed layer composed of titanium (IV) butoxide (TBO) as a precursor in an HCl solution. To reduce the amount of toxic substances used in this work, a minimal amount of HCl was used. On a larger scale, this method would require less precursor and therefore be a cost-savings. The aim of the present work is to achieve high crystalline orientations of tio 2 nRs for low quantities of both tBo precursor and Hcl solutions. Results showed that the 0.7% TBO TiO 2 NRs after 1.5 h of hydrothermal treatment exhibited the optimal crystalline orientation along [001] while the (002) plane is the dominant facet. The results demonstrate high transmittance of visible light and well-formed crystalline structures that offer a fast electron pathway along the length of the tio 2 NRs with less grain boundaries. Lastly, TiO 2 nRs and their growth mechanism are discussed. This work offers a promising hydrothermal method for growing wellaligned tio 2 single-crystal NRs that can be employed in solar cell applications. There is a growing demand for new materials to use in applications that meet today's energy and environmental challenges. In particular, wide band gap semiconductors, using very promising materials, are demonstrating impressive properties for example, high electron mobility, large band gaps and reasonably good conductivity. Among semiconducting wide band-gap materials, titanium dioxide (TiO 2) and zinc oxide (ZnO) are alternative materials used as electron transporting layers with suitable energy levels relative to Perovskite solar cells (PSC). Due to the superior electron transfer capability of each material, which is a crucial factor for PSC performance, many approaches have been found allowing TiO 2 and ZnO to be used together to enhance the overall power conversion efficiency (PCE) of PSCs. Even though ZnO layers exhibit higher electron mobility compared to TiO 2 , ZnO-based PSCs exhibit poor stability, which is a serious problem. If a Perovskite layer is created from a composition of methyl ammonium + (CH NH) 3 3 and lead triiodide − (PbI) 3 deposited on a ZnO layer, it can easily decompose during thermal treatment. However, there is less of this thermal decomposition for Perovskite and TiO 2 interfaces. TiO 2 has an acidic surface while a ZnO surface shows basic properties with high adsorption of positive charges 1. When Perovskite is exposed on a ZnO layer, a deprotonation reaction with + CH NH 3 3 occurs which could break the ionic interaction between + CH NH 3 3 and − PbI 3 and as a result, it can obstruct the crystal formation of the Perovskite 2. TiO 2 becomes the better choice and overwhelmingly interesting for its fundamental aspects and applications as well as the main motivation of this work. Moreover, TiO 2 is an ideal candidate for the large-scale manufacture of chemicals due to its stability, non-toxicity an...
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.