During 2014 and 2015, NASA's Neutron star Interior Composition Explorer (NICER) mission proceeded successfully through Phase C, Design and Development. An X-ray (0.2-12 keV) astrophysics payload destined for the International Space Station, NICER is manifested for launch in early 2017 on the Commercial Resupply Services SpaceX-11 flight. Its scientific objectives are to investigate the internal structure, dynamics, and energetics of neutron stars, the densest objects in the universe. During Phase C, flight components including optics, detectors, the optical bench, pointing actuators, electronics, and others were subjected to environmental testing and integrated to form the flight payload. A custom-built facility was used to co-align and integrate the X-ray "concentrator" optics and silicon-drift detectors. Ground calibration provided robust performance measures of the optical (at NASA's Goddard Space Flight Center) and detector (at the Massachusetts Institute of Technology) subsystems, while comprehensive functional tests prior to payload-level environmental testing met all instrument performance requirements. We describe here the implementation of NICER's major subsystems, summarize their performance and calibration, and outline the component-level testing that was successfully applied.

This paper describes the vacuum ultraviolet (VUV) radiation durability screening testing of thin (12.7-25.4 µm) polyimide films proposed for use on the Next Generation Space Telescope (NGST) sunshield. Materials included in this screening test were Kapton ® E, Kapton ® HN, Upilex ® S, CP1, CP1 with vapour deposited aluminium (VDA) on its back surface, and CP2 with a VDA coating on its back surface. Samples were exposed to approximately 1000 equivalent sun hours (ESH) of VUV radiation and examined for changes in solar absorptance, thermal emittance, ultimate tensile strength, and elongation at failure. Changes in the solar absorptance were observed for some materials, and, additionally, significant changes in spectral reflectance were observed in the ultraviolet to visible wavelength region for all of the polyimide materials tested. Changes in the ultimate tensile strength and elongation at failure were within the experimental uncertainty for all samples. Longer exposures are needed to verify the observed trends and to develop performance predictions for these materials on the NGST sunshield.

No abstract

No abstract

No abstract