Pure BaMgSiO4:Eu(2+) phosphor, prepared by a solid state reaction method under N2 atmosphere, exhibited a strong green emission at 500 nm and a weak emission at 405 nm. Heat treatment under NH3 atmosphere causes changes in the PL intensity: the green emission at 500 nm gradually decreases and completely disappears after heat treatment for 3 h, whereas a new blue emission peak, centered at 445 nm, appears and becomes very strong. The results of the analyses with electron paramagnetic resonance (EPR), X-ray photoelectron spectroscopy (XPS), and X-ray absorption fine structure (XAFS) spectroscopy suggest that the heat treatment causes the generation of a large amount of oxygen vacancies. This resulted in the aforementioned color changes of the BaMgSiO4:Eu phosphor, which are confirmed by the results of DFT+U calculations. In particular, these calculations showed that Eu prefers to occupy Ba(3) sites, which are six coordinated to oxygen atoms. The emission at 500 nm was attributed to the 4f-5d transition energy of Eu in Ba(3) site, calculated as 2.54 eV. It was also shown that Eu 4f energy level decreases when oxygen is removed from the oxygen position adjacent to Eu, which results in a larger Eu 4f-5d transition energy and shorter wavelengths of emission peaks.

No abstract

Hydrogen is the most preferred choice as an energy source to replace the nonrenewable energy resources such as fossil fuels due to its beneficial features of abundance, ecofriendly, and outstanding gravimetric energy density. Splitting water through a proton exchange membrane (PEM) electrolyzer is a well‐known method of hydrogen production. But the major impediment is the sluggish kinetics of oxygen evolution reaction (OER). Currently, scientists are struggling to build out an acid‐stable electrocatalyst for OER with low overpotential and excellent stability. In this review, the reaction mechanism and characterization parameters of OER are introduced, and then the improvement method of metal nanocatalysts (noble metal catalysts and noble metal‐free catalysts) in acidic media is discussed. Particularly, the application of single‐atom catalysts in acidic OER is summarized, which is current researching focus. At the same time, we also briefly introduced the cluster phenomenon, which is easy to occur in the preparation of single‐atom catalysts. More importantly, we summarized the in situ characterization methods such as in situ X‐ray absorption spectroscopy, in situ X‐ray photoelectron spectroscopy, and so forth, which are conducive to further understanding of OER reaction intermediates and active sites. Finally, we put forward some opinions on the development of acidic OER.

No abstract

Photoelectrochemical water splitting has long been considered an ideal approach to producing green hydrogen by utilizing solar energy. However, the limited photocurrents and large overpotentials of the anodes seriously impede large-scale application of this technology. Here, we use an interfacial engineering strategy to construct a nanostructural photoelectrochemical catalyst by incorporating a semiconductor CdS/CdSe-MoS2 and NiFe layered double hydroxide for the oxygen evolution reaction. Impressively, the as-prepared photoelectrode requires an low potential of 1.001 V vs. reversible hydrogen electrode for a photocurrent density of 10 mA cm−2, and this is 228 mV lower than the theoretical water splitting potential (1.229 vs. reversible hydrogen electrode). Additionally, the generated current density (15 mA cm−2) of the photoelectrode at a given overpotential of 0.2 V remains at 95% after long-term testing (100 h). Operando X-ray absorption spectroscopy revealed that the formation of highly oxidized Ni species under illumination provides large photocurrent gains. This finding opens an avenue for designing high-efficiency photoelectrochemical catalysts for successive water splitting.