Lanthanide-doped upconversion nanoparticles have attracted extensive research interests due to their promising applications in various fields. However, conventional upconversion nanoparticles generally suffer from severe quenching effect, leading to extremely weak...

Ultrathin porous Co3O4 nanosheets are synthesized successfully, the thickness of which is about three unit-cell dimensions. The enhanced oxygen evolution reaction (OER) performance and electronic interaction between Co3O4 and Au is firstly reported in Co3O4 ultrathin porous nanosheets by physically mixing with Au nanoparticles. With the loading of the Au nanoparticles, the current density of ultrathin porous Co3O4 nanosheets is enhanced from 9.97 to 14.76 mA cm−2 at an overpotential of 0.5 V, and the overpotential required for 10 mA cm−2 decreases from 0.51 to 0.46 V, smaller than that of commercial IrO2 (0.54 V). Furthermore, a smaller Tafel slope and excellent durability are also obtained. Raman spectra, XPS measurement, and X-ray absorption near edge structure spectra (XANES) show that the enhanced OER ascribed to a higher Co2+/Co3+ ratio and quicker charge transfer due to the electronic interaction between Au and ultrathin Co3O4 nanosheets with low-coordinated surface, and Co2+ ions are beneficial for the formation of CoOOH active sites.